Elevated Temperature, Notched Compression Performance of Out of Autoclave Processed Composites

Curved honeycomb sandwich panels composed of carbon fiber reinforced toughened-epoxy polymer facesheets are being evaluated for potential use as payload fairing components on the NASA heavy-lift space launch system (HL-SLS). These proposed composite sandwich panels provide the most efficient aerospace launch structures, and offer mass and thermal advantages when compared with existing metallic payload fairing structures. NASA and industry are investigating recently developed carbon fiber epoxy prepreg systems which can be fabricated using out-of autoclave (OOA) processes. Specifically, OOA processes using vacuum pressure in an oven and thereby significantly reducing the cost associated with manufacturing large (up to 10 m diameter) composite structures when compared with autoclave. One of these OOA composite material systems, CYCOM(R) 5320-1, was selected for manufacture of a 1/16th scale barrel portion of the payload fairing; such that, the system could be compared with the well-characterized prepreg system, CYCOM(R) 977-3, typically processed in an autoclave. Notched compression coupons for each material were obtained from the minimum-gauge flat laminate [60/-60/0]S witness panels produced in this manufacturing study. The coupons were also conditioned to an effective moisture equilibrium point and tested according to ASTM D6484M-09 at temperatures ranging from 25 C up to 177 C. The results of this elevated temperature mechanical characterization study demonstrate that, for thin coupons, the OHC strength of the OOA laminate was equivalent to the flight certified autoclave processed composite laminates; the limitations on the elevated temperature range are hot-wet conditions up to 163 C and are only within the margins of testing error. At 25 C, both the wet and dry OOA material coupons demonstrated greater OHC failure strengths than the autoclave processed material laminates. These results indicate a substantial improvement in OOA material development and processing since previous studies have consistently reported OOA material strengths on par or below those of autoclave processed composite laminates.

[1]  T. Zimmerman,et al.  Face-Sheet Quality Analysis and Thermo-Physical Property Characterization of OOA and Autoclave Panels , 2012 .

[2]  T. Zimmerman,et al.  Large Scale Composite Manufacturing for Heavy Lift Launch Vehicles , 2012 .

[3]  J. Fikes,et al.  Comparison of Autoclave and Out-of-Autoclave Composites , 2010 .

[4]  A. Nettles Hot/Wet Open Hole Compression Strength of Carbon/Epoxy Laminates for Launch Vehicle Applications , 2009 .

[5]  Constantinos Soutis,et al.  Measuring the notched compressive strength of composite laminates : Specimen size effects , 2008 .

[6]  B. Cox,et al.  Towards rapid screening of new composite matrix resins , 2006 .

[7]  Lorenzo Iannucci,et al.  An energy based damage model for thin laminated composites , 2006 .

[8]  Hiroshi Suemasu,et al.  On Failure Mechanisms of Composite Laminates with an Open Hole Subjected to Compressive Load , 2006 .

[9]  Damodar R. Ambur,et al.  Damage Progression in Buckle-Resistant Notched Composite Plates Loaded in Uniaxial Compression , 2001 .

[10]  J. Tomblin,et al.  MATERIAL QUALIFICATION AND EQUIVALENCY FOR POLYMER MATRIX COMPOSITE MATERIAL SYSTEMS. , 2001 .

[11]  Constantinos Soutis,et al.  A method for predicting the fracture toughness of CFRP laminates failing by fibre microbuckling , 2000 .

[12]  Constantinos Soutis,et al.  Predicting the compressive engineering performance of carbon fibre-reinforced plastics , 2000 .

[13]  Sérgio Frascino Müller de Almeida,et al.  Effect of void content on the strength of composite laminates , 1994 .

[14]  Constantinos Soutis Damage tolerance of open-hole CFRP laminates loaded in compression , 1994 .

[15]  G. C. Grimes,et al.  Tape composite material allowables application in airframe design/analysis , 1993 .

[16]  J. Schaff,et al.  Predicting The Compression Strength Of Impact-Damaged Sandwich Panels , 1990 .

[17]  John Morton,et al.  The effect of hygrothermal environments upon the tensile and compressive strengths of notched CFRP laminates. Part 2: Fatigue loading , 1990 .

[18]  Y. Kojima Aluminum-Lithium alloys. , 1989 .

[19]  R. Ritchie,et al.  Fatigue crack propagation in aluminum-lithium alloys , 1989 .

[20]  R. Ritchie,et al.  Fatigue crack propagation in aluminum- lithium alloy 2090: Part I. long crack behavior , 1988 .

[21]  R. O. Ritchie,et al.  Fatigue crack propagation in aluminum-lithium alloy 2090: Part II. small crack behavior , 1988 .

[22]  I. Raju,et al.  Strain-energy-release rate analysis of delamination around an open hole in composite laminates , 1984 .

[23]  D. Purslow,et al.  The effect of environment on the compression strength of notched CFRP — a fractographic investigation , 1984 .

[24]  R. Potter,et al.  The environmental degradation of notched CFRP in compression , 1983 .

[25]  P. E. Mcgowan,et al.  Effect of orthotropic properties and panel width on the compression strength of graphite-epoxy laminates with holes , 1982 .