Microfluidization, time-effective and solvent free processing of nanoparticle containing thermosetting matrix resin suspensions for producing composites with enhanced thermal properties

Abstract Dispersion of low content (0.1 wt.%) of multi walled carbon nanotubes (MWCNTs) in an epoxy resin through microfluidization was brought under spotlight as a case study. For the sake of performance comparison, epoxy resin suspension with the same MWCNT content was also produced through sonication, and the energy consumed to disperse MWCNTs in the epoxy resin remained the same for the both processes. At the equal energy consumption level, preparing the resin suspension through microfluidization was determined to take approximately 4.5 min, which is about 9 times lower than it takes for the same suspension to be prepared through sonication. Following cure of the prepared suspensions, thermal and thermo-mechanical properties of the resulting composites were systematically investigated. As a result, glass transition temperature (Tg) of the neat epoxy and its composites produced by sonication and microfluidization were determined to be 78 ± 3, 83 ± 5 and 88 ± 4 °C, respectively. Moreover, thermal expansion coefficient (CTE) of the epoxy resin was reduced by 7% when it was blended with MWCNTs through microfluidization, while no significant change was observed in the corresponding CTE value when through sonication. Thermomechanical testing findings implied about 5% and 10% improvement in storage and loss modulus values of the composites produced by microfluidization over by sonication. Transmission electron microscopy (TEM) examination showed that MWCNTs were more homogenously and individually dispersed in the epoxy resin by retaining their initial aspect ratio through microfluidization. Scanning electron microscopy (SEM) examination revealed that composite fracture surface morphology significantly varied, depending to large extent on the type of the process used. Based on the results obtained, it was proposed that microfluidization might pave the way for cost-and-time effective solvent-free processing of nanoparticle modified thermosetting resin suspensions, especially including those that could be promisingly used as matrix constituent for manufacturing fabric reinforced composites with multi-functional properties.

[1]  Thomai Panagiotou,et al.  Production of Norfloxacin Nanosuspensions Using Microfluidics Reaction Technology through Solvent/Antisolvent Crystallization , 2009 .

[2]  Marino Quaresimin,et al.  Glass-fibre-reinforced composites with enhanced mechanical and electrical properties – Benefits and limitations of a nanoparticle modified matrix , 2006 .

[3]  Charles M. Lieber,et al.  Nanobeam Mechanics: Elasticity, Strength, and Toughness of Nanorods and Nanotubes , 1997 .

[4]  Milo S. P. Shaffer,et al.  Development of a dispersion process for carbon nanotubes in an epoxy matrix and the resulting electrical properties , 1999 .

[5]  Young Hee Lee,et al.  Crystalline Ropes of Metallic Carbon Nanotubes , 1996, Science.

[6]  Bodo Fiedler,et al.  Influence of nano-modification on the mechanical and electrical properties of conventional fibre-reinforced composites , 2005 .

[7]  K. Schulte,et al.  Electric field effects on CNTs/vinyl ester suspensions and the resulting electrical and thermal composite properties , 2010 .

[8]  M. A. Gómez,et al.  Solvent-free preparation of high-toughness epoxy--SWNT composite materials. , 2011, ACS applied materials & interfaces.

[9]  David Tománek,et al.  Structural rigidity and low frequency vibrational modes of long carbon tubules , 1993 .

[10]  Karl Schulte,et al.  Surface modified multi-walled carbon nanotubes in CNT/epoxy-composites , 2003 .

[11]  Chuck Zhang,et al.  Preparative Ultracentrifuge Method for Characterization of Carbon Nanotube Dispersions , 2008 .

[12]  J. Rogers,et al.  Ultrathin Films of Single‐Walled Carbon Nanotubes for Electronics and Sensors: A Review of Fundamental and Applied Aspects , 2009 .

[13]  Ben Wang,et al.  The exfoliation of SWCNT bundles examined by simultaneous Raman scattering and photoluminescence spectroscopy , 2009 .

[14]  T. Chou,et al.  Advances in the science and technology of carbon nanotubes and their composites: a review , 2001 .

[15]  Rodney S. Ruoff,et al.  Mechanical and thermal properties of carbon nanotubes , 1995 .

[16]  K. Schulte,et al.  Mode I and mode II fracture toughness of E-glass non-crimp fabric/carbon nanotube (CNT) modified polymer based composites , 2008 .

[17]  K. Drechsler,et al.  Evaluating vibration assisted vacuum infusion processing of hexagonal boron nitride sheet modified carbon fabric/epoxy composites in terms of interlaminar shear strength and void content , 2016 .

[18]  H. Yurdakul,et al.  Nanoscopic characterization of two-dimensional (2D) boron nitride nanosheets (BNNSs) produced by microfluidization , 2012 .

[19]  Bodo Fiedler,et al.  Influence of different carbon nanotubes on the mechanical properties of epoxy matrix composites – A comparative study , 2005 .

[20]  P. Ajayan,et al.  Aligned Carbon Nanotube Arrays Formed by Cutting a Polymer Resin—Nanotube Composite , 1994, Science.

[21]  K. Schulte,et al.  Carbon nanotube-reinforced epoxy-composites: enhanced stiffness and fracture toughness at low nanotube content , 2004 .

[22]  K. Schulte,et al.  Thermal curing behavior of MWCNT modified vinyl ester‐polyester resin suspensions prepared with 3‐roll milling technique , 2009 .

[23]  T. Panagiotou,et al.  Deagglomeration and Dispersion of Carbon Nanotubes Using MicrofluidizerTM High Shear Fluid Processors , 2008 .

[24]  M. Strano,et al.  Sonication-induced changes in chiral distribution: A complication in the use of single-walled carbon nanotube fluorescence for determining species distribution , 2005 .

[25]  A. Díez-Pascual,et al.  Covalent functionalization of MWCNTs with poly(p-phenylene sulphide) oligomers: a route to the efficient integration through a chemical approach , 2012 .