Thermal Spraying of MCrAlY Overlay Coating Using New Ethanol-Fueled HVOF Gun

The MCrAlY overlay coatings are widely used for high-temperature protection of hot section part of gas turbines and jet engines. This type of coatings are usually thermally sprayed using APS (Atmospheric Plasma Spraying), LPPS (Low Pressure Plasma Spraying) as well as HVOF (High Velocity Oxygen Fuel) methods. In present article the newly developed ethanol based HVOF gun was used for production of this type of coatings. The stainless steel 18-8 type was used as a base material. The AMDRY 386 (Oerlikon-Metco) NiCrAlY powder was used for coatings production. In the research different oxygen (400, 500, 600 NLPM) and ethanol (16.5, 18.3, 21.3, 23.6 and 26.6 dm3/h) flow ratio were selected for experimental processes. The powder feed ratio was also changed during process. After deposition the microstructural assessment using Scanning Electron Microscopy and chemical composition analysis using EDS method were conducted. The obtained results showed that coating was above 100 μm thick depending on the process parameters. The low concentration of pores and oxides was also observed on coatings cross-section. Using of ethanol HVOF gun enables to form good quality MCrAlY coatings with 50% reduction of oxygen consumption in comparison with conventional HP/HVOF torch using kerosene such as JP 5000. The other benefit of its using is lower CO2 emission and lower concentration of carbon in coating in comparison with classic JP 5000 HVOF gun. The ethanol HVOF is a promising technology and might be considered as an replacement of LPPS and HVOF process for production of MCrAlY type of coatings.

[1]  H. Liao,et al.  Novel liquid fuel HVOF torches fueled with ethanol: relationships between in-flight particle characteristics and properties of WC-10Co-4Cr coatings , 2021 .

[2]  M. Góral,et al.  The Isothermal Oxidation of MCrAlY Protective Coatings , 2021 .

[3]  A. C. Karaoglanli,et al.  Comparison of microstructure and oxidation behavior of CoNiCrAlY coatings produced by APS, SSAPS, D-gun, HVOF and CGDS techniques , 2020 .

[4]  A. Zakeri,et al.  Impact of MCrAlY feedstock powder modification by high-energy ball milling on the microstructure and high-temperature oxidation performance of HVOF-sprayed coatings , 2020 .

[5]  W. Nowak,et al.  Durability of underaluminized thermal barrier coatings during exposure at high temperature , 2020 .

[6]  H. Myalska,et al.  Effect of nano-sized TiC powder on microstructure and the corrosion resistance of WC-Co thermal spray coatings , 2017 .

[7]  T. Chmielewski,et al.  Warunki natryskiwania HVOF powłoki Cr3C2-NiCr na stal 316L , 2017 .

[8]  T. Chmielewski,et al.  HVOF spraying process conditions of coating Cr3C2-NiCr deposited onto 316L steel , 2017 .

[9]  M. Góral,et al.  The Influence of LPPS Process Parameters on Porosity and Microstructure of MCrAlY Coatings , 2016 .

[10]  P. C. Monteiro,et al.  Microstructure of TBC Coatings Deposited by HVAF and PS-PVD Methods , 2015 .

[11]  K. Dychtoń,et al.  Influence of Low Pressure Plasma Spraying Parameters on MCrAlY Bond Coat and its Microstructure , 2013 .

[12]  A. Lavacchi,et al.  A comparative study of high velocity oxygen fuel, vacuum plasma spray, and axial plasma spray for the deposition of CoNiCrAlY bond coat alloy , 2003 .

[13]  Y. Tamarin Protective Coatings for Turbine Blades , 2002 .