Dissolution and Migration of Platinum in PEMFCs Investigated for Start/Stop Cycling and High Potential Degradation

Dissolution and migration of platinum due to start/stop degradation and increased cathode potentials were studied for commercial membrane electrode assemblies (MEA). The chosen conditions closely mimic real situations in automotive operation. In start/stop tests, we observed a strongly enhanced platinum dissolution due to the dynamic interplay of repeated cell start-up and consecutive normal fuel cell operation, which is related to platinum oxidation (start-up) and reduction (normal operation) cycles. Consequently, the performed test protocols distinguish between dynamic and static load profiles. Electrochemical investigations before and after degradation monitor the loss in cell performance. Since electron microscopy offers the unique possibility to unravel and distinguish degradation due to carbon corrosion and agglomeration or platinum dissolution, a focus was set on this method. For the start/stop MEA pronounced platinum dissolution accompanied by the formation of large platinum precipitations in the membrane was found. Carbon corrosion was also observed, but did not lead to a significantly reduced porosity and loss in platinum dispersion. In contrast, the MEA which was exposed to high constant potentials exhibited severe damage to the 3D cathode structure due to carbon corrosion. However, no pronounced platinum dissolution was observed and only few Pt precipitations were found in the membrane itself.

[1]  Michael Hicks,et al.  Ex Situ and In Situ Stability Studies of PEMFC Catalysts Effect of Carbon Type and Humidification on Degradation of the Carbon , 2005 .

[2]  Frédéric Maillard,et al.  Membrane and Active Layer Degradation upon PEMFC Steady-State Operation I. Platinum Dissolution and Redistribution within the MEA , 2007 .

[3]  Hartmut Fuess,et al.  Spatially resolved degradation effects in membrane-electrode-assemblies of vehicle aged polymer electrolyte membrane fuel cell stacks , 2009 .

[4]  Hubert A. Gasteiger,et al.  The Impact of Carbon Stability on PEM Fuel Cell Startup and Shutdown Voltage Degradation , 2006 .

[5]  Michael P. Balogh,et al.  Investigation of thermal and electrochemical degradation of fuel cell catalysts , 2006 .

[6]  Tomoki Akita,et al.  Platinum dissolution and deposition in the polymer electrolyte membrane of a PEM fuel cell as studied by potential cycling. , 2006, Physical chemistry chemical physics : PCCP.

[7]  S. D. Fraser,et al.  Polarization study of a PEMFC with four reference electrodes at hydrogen starvation conditions , 2008 .

[8]  Geping Yin,et al.  Durability studies on performance degradation of Pt/C catalysts of proton exchange membrane fuel cell , 2009 .

[9]  Shimshon Gottesfeld,et al.  Surface Area Loss of Supported Platinum in Polymer Electrolyte Fuel Cells , 1993 .

[10]  Lawrence F. Allard,et al.  Preparation of Cross-Sectional Samples of Proton Exchange Membrane Fuel Cells by Ultramicrotomy for TEM , 2003 .

[11]  Zhongwei Chen,et al.  Durability investigation of carbon nanotube as catalyst support for proton exchange membrane fuel cell , 2006 .

[12]  Kazuhiko Shinohara,et al.  Membrane degradation mechanism during open-circuit voltage hold test , 2008 .

[13]  V. Birss,et al.  Platinum oxide film formation—reduction: an in-situ mass measurement study , 1993 .

[14]  Robert M. Darling,et al.  Kinetic Model of Platinum Dissolution in PEMFCs , 2003 .

[15]  L. J. Bregoli,et al.  A Reverse-Current Decay Mechanism for Fuel Cells , 2005 .

[16]  Geping Yin,et al.  Durability Study of Pt ∕ C and Pt ∕ CNTs Catalysts under Simulated PEM Fuel Cell Conditions , 2006 .

[17]  T. Jarvi,et al.  Electrocatalytic corrosion of carbon support in PEMFC cathodes , 2004 .

[18]  David L. Wood,et al.  PEM fuel cell electrocatalyst durability measurements , 2006 .

[19]  Anusorn Kongkanand,et al.  Single-wall carbon nanotubes supported platinum nanoparticles with improved electrocatalytic activity for oxygen reduction reaction. , 2006, Langmuir : the ACS journal of surfaces and colloids.

[20]  Tomoki Akita,et al.  Characteristics of a Platinum Black Catalyst Layer with Regard to Platinum Dissolution Phenomena in a Membrane Electrode Assembly , 2006 .

[21]  H. Gasteiger,et al.  Catalyst Development Needs and Pathways for Automotive PEM Fuel Cells , 2006 .

[22]  Brian Theobald,et al.  An investigation into factors affecting the stability of carbons and carbon supported platinum and platinum/cobalt alloy catalysts during 1.2 V potentiostatic hold regimes at a range of temperatures , 2007 .

[23]  Hubert A. Gasteiger,et al.  Instability of Pt ∕ C Electrocatalysts in Proton Exchange Membrane Fuel Cells A Mechanistic Investigation , 2005 .

[24]  Lim Kim,et al.  Dissolution and migration of platinum after long-term operation of a polymer electrolyte fuel cell under various conditions , 2008 .

[25]  S. Maaß,et al.  Carbon support oxidation in PEM fuel cell cathodes , 2008 .

[26]  T. Jarvi,et al.  Characterization of Vulcan Electrochemically Oxidized under Simulated PEM Fuel Cell Conditions , 2004 .

[27]  Vat Dam,et al.  The Stability of PEMFC Electrodes Platinum Dissolution vs Potential and Temperature Investigated by Quartz Crystal Microbalance , 2007 .

[28]  Héctor R. Colón-Mercado,et al.  Stability of platinum based alloy cathode catalysts in PEM fuel cells , 2006 .

[29]  Yong Wang,et al.  The influence of the electrochemical stressing (potential step and potential-static holding) on the degradation of polymer electrolyte membrane fuel cell electrocatalysts , 2008 .

[30]  Hansung Kim,et al.  Effect of operating conditions on carbon corrosion in polymer electrolyte membrane fuel cells , 2009 .

[31]  Loreto Daza,et al.  High surface area graphite as alternative support for proton exchange membrane fuel cell catalysts , 2009 .

[32]  T. Murahashi,et al.  Change of Pt Distribution in the Active Components of Phosphoric Acid Fuel Cell , 1988 .