Spherical and acicular representation of hydrates in a micromechanical model for cement paste: prediction of early-age elasticity and strength

Early-age stiffness and strength evolution of cement paste is studied in the framework of continuum micromechanics. Based on the self-consistent scheme, elastic and strength properties are upscaled from the scale of several micrometers up to the scale of several hundreds or thousands of micrometers. Four material phases are considered: clinker, hydration products, water and air. We assign a spherical geometry to clinker grains and pores, while we investigate both spherical and acicular (needle-type) shapes as geometrical representation of the micrometer-sized hydration products. As regards macroscopic poromechanical boundary conditions, two extreme cases are considered: drained conditions and sealed conditions, respectively. These choices allow for studying the influence of (i) the morphological representation of hydrates, and of (ii) the bulk stiffness of water, on the micromechanical prediction of early-age behavior of cement paste, including setting and the hydration-dependent evolutions of both elastic stiffness and uniaxial compressive strength. The newly proposed strength model is based on a von Mises-type elastic limit criterion for individual hydrates. Corresponding deviatoric stress peaks within hydrates are estimated through quadratic stress averages. In this way, the micromechanical strength criterion is formulated in terms of macroscopic loading (stresses or strains, respectively). Model-predicted elasticity and strength evolutions are compared with data from experimental testing of cement pastes with water–cement ratios ranging from 0.35 to 0.60. Satisfactory agreement between model predictions and experiments allows for two conclusions: the morphology of hydrates significantly influences micromechanics-based elastic stiffness estimates of cement paste particularly at very early ages, whereas elastic properties of mature cement paste can be estimated reliably on the basis of both spherical or acicular shaped hydrates. The development of a reliable strength model, however, requires consideration of hydrates as non-spherical particles, no matter what age of cement paste is considered.

[1]  Luc Dormieux,et al.  Elements of poro-micromechanics applied to concrete , 2004 .

[2]  H. Jennings,et al.  A model for two types of calcium silicate hydrate in the microstructure of Portland cement pastes , 2000 .

[3]  F. Ulm,et al.  The effect of two types of C-S-H on the elasticity of cement-based materials: Results from nanoindentation and micromechanical modeling , 2004 .

[4]  P. H. Feenstra,et al.  A composite plasticity model for concrete , 1996 .

[5]  J. Salençon.  Handbook of continuum mechanics , 2001 .

[6]  Franz-Josef Ulm,et al.  Is concrete a poromechanics materials?—A multiscale investigation of poroelastic properties , 2004 .

[7]  Christian Hellmich,et al.  Micromechanics of crystal interfaces in polycrystalline solid phases of porous media: fundamentals and application to strength of hydroxyapatite biomaterials , 2007 .

[8]  André Zaoui,et al.  Structural morphology and constitutive behaviour of microheterogeneous materials , 1997 .

[9]  Christian Hellmich,et al.  Drained and Undrained Poroelastic Properties of Healthy and Pathological Bone: A Poro-Micromechanical Investigation , 2005 .

[10]  Alain Molinari,et al.  Residual stresses in polycrystals as influenced by grain shape and texture , 1993 .

[11]  E. Lesniewska,et al.  Study of C-S-H growth on C3S surface during its early hydration , 2005 .

[12]  J. Willis,et al.  The effect of spatial distribution on the effective behavior of composite materials and cracked media , 1995 .

[13]  Valery M. Levin,et al.  Effective elastic properties of matrix composites with transversely-isotropic phases , 2005 .

[14]  Gilles Chanvillard,et al.  Modelling Elasticity of a Hydrating Cement Paste , 2007 .

[15]  W. Kreher,et al.  Residual stresses and stored elastic energy of composites and polycrystals , 1990 .

[16]  Surendra P. Shah,et al.  Modeling the linear elastic properties of Portland cement paste , 2005 .

[17]  Josef Tritthart,et al.  Pore solution analysis of cement pastes and nanostructural investigations of hydrated C3S , 2003 .

[18]  Sergey G. Psakhie,et al.  Movable cellular automata method for simulating materials with mesostructure , 2001 .

[19]  Olivier Coussy,et al.  Strength growth as chemo-plastic hardening in early age concrete , 1996 .

[20]  N. Laws,et al.  The determination of stress and strain concentrations at an ellipsoidal inclusion in an anisotropic material , 1977 .

[21]  Franz-Josef Ulm,et al.  Effect of Inclusions on Friction Coefficient of Highly Filled Composite Materials , 2002 .

[22]  Franz-Josef Ulm,et al.  Microporomechanics: Dormieux/Microporomechanics , 2006 .

[23]  Christian Hellmich,et al.  Shotcrete elasticity revisited in the framework of continuum micromechanics : From submicron to meter level , 2005 .

[24]  Bernhard A. Schrefler,et al.  Numerical analysis of hygro-thermal behaviour and damage of concrete at high temperature , 1999 .

[25]  Christian Hellmich,et al.  Mineral–collagen interactions in elasticity of bone ultrastructure – a continuum micromechanics approach , 2004 .

[26]  Bernhard A. Schrefler,et al.  Hygro‐thermo‐chemo‐mechanical modelling of concrete at early ages and beyond. Part I: hydration and hygro‐thermal phenomena , 2006 .

[27]  Z. Hashin.  Analysis of Composite Materials—A Survey , 1983 .

[28]  Christian Hellmich,et al.  Mechanical behavior of hydroxyapatite biomaterials: an experimentally validated micromechanical model for elasticity and strength. , 2009, Journal of biomedical materials research. Part A.

[29]  Y. Benveniste,et al.  A new approach to the application of Mori-Tanaka's theory in composite materials , 1987 .

[30]  F. Cohen Tenoudji,et al.  Mechanical properties of cement pastes and mortars at early ages: Evolution with time and degree of hydration , 1996 .

[31]  Zhihui Sun,et al.  Microstructure and early-age properties of Portland cement paste - Effects of connectivity of solid phases , 2005 .

[32]  L. Dormieux,et al.  A micromechanical approach to the strength criterion of Drucker‐Prager materials reinforced by rigid inclusions , 2004 .

[33]  J. D. Eshelby.  The determination of the elastic field of an ellipsoidal inclusion, and related problems , 1957, Proceedings of the Royal Society of London. Series A. Mathematical and Physical Sciences.

[34]  A. Stroud.  Approximate calculation of multiple integrals , 1973 .

[35]  George S. K. Wong,et al.  Erratum: Speed of sound in pure water as a function of temperature [J. Acoust. Soc. Am. 93, 1609–1612 (1993)] , 1996 .

[36]  R. Hill.  Elastic properties of reinforced solids: some theoretical principles , 1963 .

[37]  Vít S˘milauer,et al.  Microstructure-based micromechanical prediction of elastic properties in hydrating cement paste , 2006 .

[38]  B. Bary,et al.  Influence of inclusion shapes on the effective linear elastic properties of hardened cement pastes , 2006 .

[39]  David Darwin,et al.  STRAIN-RATE SENSITIVE BEHAVIOR OF CEMENT PASTE AND MORTAR IN COMPRESSION , 1990 .

[40]  Jean-François Barthélémy,et al.  Détermination du critère de rupture macroscopique d'un milieu poreux par homogénéisation non linéaire , 2003 .

[41]  Alain Molinari,et al.  Micromechanical approach to the behavior of poroelastic materials , 2002 .

[42]  George S. K. Wong,et al.  Speed of sound in pure water as a function of temperature , 1993 .

[43]  Zdeněk P. Bažant,et al.  Creep, shrinkage and durability mechanics of concrete and other quasi-brittle materials : proceedings of the sixth international conference CONCREEP-6@MIT, 20-22 August 2001, Cambridge(MA), USA , 2001 .

[44]  I. Sevostianov,et al.  On the modeling and design of piezocomposites with prescribed properties , 2001 .

[45]  Xanthippi Markenscoff,et al.  Collected Works of J. D. Eshelby , 2006 .

[46]  J. Maso,et al.  Hardened portland cement pastes, modelisation of the micro-structure and evolution laws of mechanical properties II- compressive strength law , 1984 .

[47]  Stefan Scheiner,et al.  From micron-sized needle-shaped hydrates to meter-sized shotcrete tunnel shells: micromechanical upscaling of stiffness and strength of hydrating shotcrete , 2008 .

[48]  J. Granju,et al.  RELATION BETWEEN THE HYDRATION STATE AND THE COMPRESSIVE STRENGTH OF HARDENED PORTLAND CEMENT PASTES , 1989 .

[49]  L. Dormieux,et al.  Micromechanical approach to the modelling of compaction at large strains , 2003, Poromechanics II.

[50]  Pierre Suquet,et al.  Continuum Micromechanics , 1997, Encyclopedia of Continuum Mechanics.

[51]  E. Kröner.  Berechnung der elastischen Konstanten des Vielkristalls aus den Konstanten des Einkristalls , 1958 .

[52]  M. Biot.  THEORY OF ELASTICITY AND CONSOLIDATION FOR A POROUS ANISOTROPIC SOLID , 1955 .

[53]  K. Tanaka,et al.  Average stress in matrix and average elastic energy of materials with misfitting inclusions , 1973 .

[54]  A. Fritsch,et al.  Porous polycrystals built up by uniformly and axisymmetrically oriented needles: homogenization of elastic properties , 2006 .

[55]  J. D. Eshelby,et al.  Collected Works Of J D Eshelby The Mechanics Of Defects And Inhomogeneities , 2006 .

[56]  Franz-Josef Ulm,et al.  A multiscale micromechanics-hydration model for the early-age elastic properties of cement-based materials , 2003 .

[57]  A. Zaoui.  Continuum Micromechanics: Survey , 2002 .