Study of surface quality in high speed turning of Inconel 718 with uncoated and coated CBN tools

Inconel 718 is known to be among the most difficult-to-machine materials due to its special properties which cause the short tool life and severe surface damages. The properties, which are responsible for poor machinability, include rapid work hardening during machining; tendency to weld with the tool material at high temperature generated during machining; the tendency to form a built-up edge during machining; and the presence of hard carbides, such as titanium carbide and niobium carbide, in their microstructure. Conventional method of machining Inconel 718 with cemented carbide tool restricts the cutting speed to a maximum 30 m/min due to the lower hot hardness of carbide tool, high temperature strength and low thermal conductivity of Inconel 718. The introduction of new coated carbide tools has increased cutting speed to 100 m/min; nevertheless, the time required to machine this alloy is still considerably high. High speed machining using advanced tool material, such as CBN, is one possible alternative for improving the productivity of this material due to its higher hot hardness in comparison with carbide tool. This paper specifically deals with surface quality generated under high speed finishing turning conditions on age-hardened Inconel 718 with focus on surface roughness, metallographic analysis of surface layer and surface damages produced by machining. Both coated and uncoated CBN tools were used in the tests, and a comparison between surfaces generated by both tools was also discussed.

[1]  M. A. Mannan,et al.  MACHINABILITY OF NICKEL-BASED HIGH TEMPERATURE ALLOYS , 2000 .

[2]  Q. Yang,et al.  Formation of nanocrystalline niobium carbide (NbC) with a convenient route at low temperature , 2009 .

[3]  Y. K. Chou,et al.  Tool nose radius effects on finish hard turning , 2004 .

[4]  S. Baker.  The Analysis of Depth-Sensing Indentation Data , 1993 .

[5]  R. Reed.  The Superalloys by Roger C. Reed , 2006 .

[6]  E. Ezugwu,et al.  An overview of the machinability of aeroengine alloys , 2003 .

[7]  Bin Zou,et al.  Study on surface damages caused by turning NiCr20TiAl nickel-based alloy , 2009 .

[8]  M. Billy,et al.  Oxidation of titanium nitride in oxygen: Behavior of TiN0.83 and TiN0.79 plates , 1979 .

[9]  R. Reed.  The Superalloys: Fundamentals and Applications , 2006 .

[10]  T. Kitagawa,et al.  Temperature and wear of cutting tools in high-speed machining of Inconel 718 and Ti6Al6V2Sn , 1997 .

[11]  M. Iwaki,et al.  Improvement of high-temperature oxidation resistance of titanium nitride and titanium carbide films by aluminum ion implantation , 1998 .

[12]  David K. Aspinwall,et al.  Tool life when high speed ball nose end milling Inconel 718 , 2001 .

[13]  Hossam A. Kishawy,et al.  Surface Integrity of Die Material in High Speed Hard Machining, Part 1: Micrographical Analysis , 2000 .

[14]  Mahmudur Rahman,et al.  An investigation of cutting forces and surface damage in high-speed turning of inconel 718 , 2007 .

[15]  A. Sadat,et al.  Surface integrity of inconel-718 nickel-base superalloy using controlled and natural contact length tools. part I: Lubricated , 1992 .

[16]  Keith Ridgway,et al.  Tool life and surface integrity aspects when drilling and hole making in Inconel 718 , 2008 .

[17]  Marco J. Starink,et al.  Short crack initiation and growth at 600 °C in notched specimens of Inconel718 , 2003 .

[18]  J. Nowacki.  Role of copper in iron–iron boride cermets , 2001 .

[19]  S. Jeelani,et al.  Surface Integrity in Machining AISI 4340 Steel , 1976 .

[20]  Titus. B. Watmon,et al.  Coating Cutting Tools with Hard Substance Lowers Friction Co-efficient and Improves Tool Life - A Review , 2010 .