Transformation of mackinawite to greigite: An in situ X-ray powder diffraction and transmission electron microscope study

Abstract Synthetic mackinawite (tetragonal FeS) has been found to transform rapidly to greigite (Fe3S4) above ∼373 K during heating experiments, as observed by in situ X-ray diffraction. Using monochromatic synchrotron radiation (λ = 0.60233 Å), we measured the unit-cell parameters of both synthetic mackinawite between 293 and 453 K and of greigite formed from this mackinawite between 293 and 593 K. The coefficients of thermal expansion for mackinawite are α1 = α2 = (1.36 ± 6 0.11) × 10-5, α3 = (2.98 ± 0.12) × 10-5, and αvol = (5.67 ± 0.19) × 10-5 between 293 and 453 K. The coefficients of thermal expansion for greigite are α1 = α2 = α3 = (1.63 ± 0.15) × 10-5, and αvol = (4.86 ± 0.25) x 10-5 between 293 and 593 K. On further heating in situ, we observed the reaction greigite → pyrrhotite + magnetite. Partial transformation of mackinawite to greigite was also observed using transmission electron microscopy (TEM) following in situ heating. Electron diffraction patterns show that (001) of mackinawite is parallel to (001) of greigite, and [110] of mackinawite is parallel to [100] of greigite. This orientation relationship confirms that the cubic closepacked S array in mackinawite is retained in greigite and implies that oxidation of some Fe2+ in mackinawite drives rearrangement of Fe to form the new phase. Small regions of the crystallites show Moiré fringes resulting from the lattice mismatch between mackinawite and greigite. Electron diffraction patterns of mackinawite subjected to prolonged exposure to the atmosphere also show faint spots corresponding to greigite. We propose that in these experiments surplus Fe is accommodated by reaction with either adsorbed O2 or H2O to form amorphous nanophase Fe-O(H). Because greigite is so easily formed by oxidation from mackinawite, greigite should be an important precursor for pyrite nucleation, although any orientation relationship between greigite and pyrite remains to be determined.

[1]  F. Grønvold,et al.  Phase and Structural Relations in the System Iron Tellurium. , 1954 .

[2]  R. Frankel,et al.  Biomineralization of ferrimagnetic greigite (Fe3S4) and iron pyrite (FeS2) in a magnetotactic bacterium , 1990, Nature.

[3]  S. Scott,et al.  Phase relations involving pyrrhotite below 350 degrees C , 1982 .

[4]  F. Grønvold,et al.  Heat Capacities and Thermodynamic Properties of the Iron Selenides Fe1.04Se, Fe7Se8, and Fe3Se4 from 298 to 1050 degrees K. , 1968 .

[5]  K. J. Gallagher,et al.  Mechanism of Oxidation of Magnetite to γ-Fe2O3 , 1968, Nature.

[6]  P. Taylor,et al.  On the conversion of mackinawite to greigite , 1979 .

[7]  G. Thornton,et al.  Fe3O4(111) termination of α-Fe2O3(0001) , 1994 .

[8]  R. Berner.  thermodynamic stability of sedimentary iron sulfides , 1967 .

[9]  M. Schoonen,et al.  Mechanisms of pyrite and marcasite formation from solution: III. Hydrothermal processes , 1991 .

[10]  O. Kruse.  Phase transitions and kinetics in natural FeS measured by X-ray diffraction and Moessbauer spectroscopy at elevated temperatures , 1992 .

[11]  M. Hove,et al.  Magnetite Fe3O4(111): surface structure by LEED crystallography and energetics , 1994 .

[12]  R. Berner.  Iron Sulfides Formed from Aqueous Solution at Low Temperatures and Atmospheric Pressure , 1964, The Journal of Geology.

[13]  Barbieri,et al.  Surface structure determination of an oxide film grown on a foreign substrate: Fe3O4 multilayer on Pt(111) identified by low energy electron diffraction. , 1993, Physical review letters.

[14]  Tim Holland,et al.  Unit cell refinement from powder diffraction data: the use of regression diagnostics , 1997, Mineralogical Magazine.

[15]  H. Barnes,et al.  Marcasite precipitation from hydrothermal solutions , 1986 .

[16]  B. Skinner,et al.  Greigite, the thio-spinel of iron; a new mineral , 1964 .

[17]  B. Brunhes.  AMERICAN JOURNAL OF SCIENCE. , 1896, Science.

[18]  W. Feitknecht,et al.  Über die Oxydation von Magnetit zu γ‐Fe2O3. Vorläufige Mitteilung , 1959 .

[19]  Marcos Farina,et al.  Magnetic iron-sulphur crystals from a magnetotactic microorganism , 1990, Nature.

[20]  R. Cernik,et al.  The general purpose two‐circle diffractometer on Station 9.1, Daresbury Laboratory , 1992 .

[21]  R. Krupp.  Phase relations and phase transformations between the low-temperature iron sulfides mackinawite, greigite, and smythite , 1994 .

[22]  Martin A. A. Schoonen,et al.  Reactions forming pyrite and marcasite from solution: II. Via FeS precursors below 100°C , 1991 .

[23]  I. Kaplan,et al.  Pyrite Framboid Formation; Laboratory Synthesis and Marine Sediments , 1973 .

[24]  J. Craig,et al.  Mineral chemistry of metal sulfides , 1978 .

[25]  M. Schoonen,et al.  Reactions forming pyrite and marcasite from solution: I. Nucleation of FeS2 below 100°C , 1991 .

[26]  S. Horiuchi.  Zur Umwandlung von Mackinawit (FeS) in Greigit (Fe3S4) durch Elektronenstrahlen , 1971 .

[27]  G. Luther.  Pyrite synthesis via polysulfide compounds , 1991 .

[28]  D. Vaughan,et al.  Synthesis and Rietveld crystal structure refinement of mackinawite, tetragonal FeS , 1995, Mineralogical Magazine.

[29]  D. Rickard.  Kinetics and mechanism of pyrite formation at low temperatures , 1975 .

[30]  K. Stetter,et al.  Pyrite formation linked with hydrogen evolution under anaerobic conditions , 1990, Nature.

[31]  J. Tossell,et al.  Pyrite, marcasite, and arsenopyrite type minerals: Crystal chemical and structural principles , 1981 .