Nanostructured thin solid oxide fuel cells with high power density.

Nanostructured thin film solid oxide fuel cells (SOFC) have been developed for reduced temperature operation, with high power density, and to be self reforming. A thin film electrolyte (1-2 microm thickness), e.g., yttria-stabilized zirconia (YSZ), is deposited on a nickel foil substrate. The electrolyte thin film is polycrystalline when deposited on a polycrystalline nickel foil substrate, and is (100) textured when deposited on an atomically textured nickel foil substrate. The Ni foil substrate is then converted into a porous SOFC anode by photolithographic patterning and etching to develop porosity. A composite La(0.5)Sr(0.5)CoO(3) cathode is then deposited on the thin film electrolyte. The resultant thin film hetero structure fuel cells have operated at a significantly reduced temperature: as low as 470 degrees C, with a maximum power density of 140 mW cm(-2) at 575 degrees C, and an efficiency of >50%. This drastic reduction in operating temperature for an SOFC now also allows for the use of hydrocarbon fuels without the need for a separate reformer as the nickel anode effectively dissociates hydrocarbons within this temperature range. These nanostructured fuel cells show excellent potential for high power density, small volume, high efficiency fuel cells for power generation applications.

[1]  Zongping Shao,et al.  A thermally self-sustained micro solid-oxide fuel-cell stack with high power density , 2005, Nature.

[2]  B. N. Nair,et al.  An Oriented Nanoporous Membrane Prepared by Pulsed Laser Deposition , 2005 .

[3]  N. Imanishi,et al.  Impedance spectroscopy of perovskite air electrodes for SOFC prepared by laser ablation method , 2004 .

[4]  Zongping Shao,et al.  A high-performance cathode for the next generation of solid-oxide fuel cells , 2004, Nature.

[5]  Naijuan Wu,et al.  Thin-film heterostructure solid oxide fuel cells , 2004 .

[6]  A. Boudghene Stambouli,et al.  Solid oxide fuel cells (SOFCs): a review of an environmentally clean and efficient source of energy , 2002 .

[7]  Dominic F. Lee,et al.  Epitaxial yttria-stabilized zirconia on biaxially-textured (001) Ni for YBCO coated conductor , 2000 .

[8]  N. Wu,et al.  Structure and conducting properties of La1-xSrxCoO3-δ films , 1999 .

[9]  Naijuan Wu,et al.  Pulsed laser deposition of conducting porous La-Sr-Co-O films , 1999 .

[10]  Stuart B. Adler,et al.  Mechanism and kinetics of oxygen reduction on porous La1−xSrxCoO3−δ electrodes , 1998 .

[11]  L. D. Jonghe,et al.  Reduced-Temperature Solid Oxide Fuel Cell Based on YSZ Thin-Film Electrolyte , 1997 .

[12]  John D. Budai,et al.  High critical current density superconducting tapes by epitaxial deposition of YBa2Cu3Ox thick films on biaxially textured metals , 1996 .

[13]  Sivan Kartha,et al.  Fuel Cells: Energy Conversion for the Next Century , 1994 .

[14]  Y. Zhou,et al.  The manufacturing of an electroplated Ni layer on textured Cu substrate for Cu-based HTS coated conductors , 2004 .