α phase growth and branching in titanium alloys

ABSTRACT The morphology and spatial distribution of alpha (α) precipitates have been mapped as a function of Mo content in Ti-Mo binary alloys employing a combinatorial approach. Heat-treatments were carried out on compositionally graded Ti-xMo samples processed using a rapid throughput laser engineered net shape (LENS) process. The composition space spans 1.5 at% to 6 at% Mo with ageing at 750°C, 650°C and 600°C following a β solution treatment. Three distinct regimes of α morphology and distribution were observed. These are colony-dominated microstructures originating from grain boundary α allotriomorphs, bundles of intragranular α laths, and homogeneously distributed individual fine-scale α laths. Branching of the α precipitates was observed in all these domains in a manner reminiscent of solid-state dendritic growth. The phenomenon is particularly apparent at low volume fractions of α. Similar features are present in a wide variety of alloy compositions. 3-dimensional features of such branched structures have been analysed. Simulation of the branching process by phase field methods incorporating anisotropy in the α/β interface energy and elasticity suggests that it can be initiated at growth ledges present at broad faces of the α laths, driven by the enhancement of the diffusion flux at these steps. The dependence of branching on various parameters such as supersaturation and diffusivity, and microstructural features like ledge height and distribution and the presence of adjacent α variants has been evaluated.

[1]  P. Villechaise,et al.  Microplasticity at Room Temperature in α/β Titanium Alloys , 2020, Metallurgical and Materials Transactions A.

[2]  S. Ringer,et al.  3D electron backscatter diffraction study of α lath morphology in additively manufactured Ti-6Al-4V. , 2020, Ultramicroscopy.

[3]  Yunheng Ji.  MORPHOLOGY , 1937, A Grammar of Italian Sign Language (LIS).

[4]  A. Choudhury,et al.  Dendrite tip selection during isothermal free growth in multi-component alloys: Marginal stability theories and insights from phase-field simulations , 2019, Computational Materials Science.

[5]  J. A. Francis,et al.  Titanium , 2019, Materials Science and Technology.

[6]  Yufeng Zheng,et al.  Determination of the structure of α-β interfaces in metastable β-Ti alloys , 2018 .

[7]  D. Choudhuri,et al.  Mapping the Decomposition of β to α in Composition and Temperature Space in Titanium Alloys , 2016 .

[8]  Yunzhi Wang,et al.  On variant distribution and coarsening behavior of the α phase in a metastable β titanium alloy , 2016 .

[9]  Yunzhi Wang,et al.  Microstructure and transformation texture evolution during α precipitation in polycrystalline α/β titanium alloys – A simulation study , 2015 .

[10]  Wei-jie Lu,et al.  Variant selection by dislocations during α precipitation in α/β titanium alloys , 2015 .

[11]  Yunzhi Wang,et al.  Variant selection during α precipitation in Ti–6Al–4V under the influence of local stress – A simulation study , 2013 .

[12]  James C. Williams,et al.  Perspectives on Titanium Science and Technology , 2013 .

[13]  Yunzhi Wang,et al.  Predicting equilibrium shape of precipitates as function of coherency state , 2012 .

[14]  P. Bocher,et al.  Texture and microtexture variations in a near-α titanium forged disk of bimodal microstructure , 2012 .

[15]  Jilt Sietsma,et al.  Three-dimensional analysis of microstructures in titanium , 2010 .

[16]  H. Fraser,et al.  ω-Assisted nucleation and growth of α precipitates in the Ti–5Al–5Mo–5V–3Cr–0.5Fe β titanium alloy , 2009 .

[17]  M. Jackson,et al.  Development of chevron-shaped α precipitates in Ti–5Al–5Mo–5V–3Cr , 2009 .

[18]  Nikolas Provatas,et al.  Competition between surface energy and elastic anisotropies in the growth of coherent solid-state dendrites , 2008, 0810.4978.

[19]  K. Ameyama,et al.  Reasons for Formation of Triangular α Precipitates in Ti–15V–3Cr–3Sn–3Al β Titanium Alloy , 2006 .

[20]  Britta Nestler,et al.  Crystal growth of pure substances: Phase-field simulations in comparison with analytical and experimental results , 2005 .

[21]  Y. Yoo.  Morphological instability of spherical γ′ precipitates in a nickel base superalloy , 2005 .

[22]  D. Qiu,et al.  A TEM study of the habit plane structure of intragrainular proeutectoid α precipitates in a Ti–7.26 wt%Cr alloy , 2004 .

[23]  A. N. Khan,et al.  Formation of solid-state dendrites in an alloy steel , 2004 .

[24]  Yunzhi Wang,et al.  Quantitative phase field modeling of diffusion-controlled precipitate growth and dissolution in Ti–Al–V , 2004 .

[25]  I. Qamar,et al.  Dendritic morphology observed in the solid-state precipitation in binary alloys , 1999 .

[26]  T. Furuhara,et al.  Morphology and Crystallography of α Precipitates in β Ti–Mo Binary Alloys , 1998 .

[27]  T. Furuhara,et al.  Atomic structure of interphase boundary of an a precipitate plate in a β Ti[sbnd]Cr alloy , 1995 .

[28]  G. Spanos,et al.  Sympathetic nucleation: an overview , 1995 .

[29]  C. B. Carter,et al.  Morphology of NiFe2O4 precipitation in NiO , 1992 .

[30]  H. Aaronson,et al.  Interphase boundary structures of intragranular proeutectoid α plates in a hypoeutectoid TiCr alloy , 1991 .

[31]  W. Kurz,et al.  Fundamentals of Solidification , 1990 .

[32]  C. G. Shelton,et al.  A resolution of the interface phase problem in titanium alloys , 1988 .

[33]  H. Aaronson,et al.  Overview no. 57 Morphology, crystallography and kinetics of sympathetic nucleation , 1987 .

[34]  J. Goldstein.  Principles of Thin Film X-Ray Microanalysis , 1979 .

[35]  A. G. Quarrell.  Solidification , 1965, Nature.

[36]  D. Kinderlehrer,et al.  Morphological Stability of a Particle Growing by Diffusion or Heat Flow , 1963 .

[37]  W. Rostoker,et al.  Time-Temperature-Transformation Characteristics of Titanium-Molybdenum Alloys , 1952 .