Photovoltaic Materials and Devices Based on the Alloyed Kesterite Absorber (AgxCu1–x)2ZnSnSe4

The photovoltaic absorber Cu2ZnSn(SxSe1–x)4 (CZTSSe) has attracted interest in recent years due to the earth-abundance of its constituents and the realization of high performance (12.6% efficiency). The open-circuit voltage in CZTSSe devices is believed to be limited by absorber band tailing caused by the exceptionally high density of Cu/Zn antisites. By replacing Cu in CZTSSe with Ag, whose covalent radius is ≈15% larger than that of Cu and Zn, the density of I–II antisite defects is predicted to drop. The fundamental properties of the mixed Ag-Cu kesterite compound are reported as a function of the Ag/(Ag + Cu) ratio. The extent of band tailing is shown to decrease with increasing Ag. This is verified by comparing the optical band gap extrapolated from transmission data with the position of the room-temperature photoluminescence peak; these values converge for the pure-Ag compound. Additionally, the pinning of the Fermi level in CZTSSe, attributed to heavy defect compensation and band tailing, is not observed in the pure-Ag compound, offering further evidence of improved electronic structure. Finally, a device efficiency of 10.2% is reported for a device containing 10% Ag (no antireflection coating); this compares to ≈9% (avg) efficiency for the baseline pure-Cu CZTSe.

[1]  T. Wada,et al.  Crystallographic and optical properties of (Cu, Ag)2ZnSnS4 and (Cu, Ag)2ZnSnSe4 solid solutions , 2015 .

[2]  O. Gunawan,et al.  A Diamagnetic Trap with 1D Camelback Potential , 2014, 1405.5220.

[3]  W. Shafarman,et al.  Bulk and metastable defects in CuIn1−xGaxSe2 thin films using drive-level capacitance profiling , 2004 .

[4]  Yue Hao,et al.  A simple and efficient solar cell parameter extraction method from a single current-voltage curve , 2011 .

[5]  Wei Wang,et al.  Device Characteristics of CZTSSe Thin‐Film Solar Cells with 12.6% Efficiency , 2014 .

[6]  Tayfun Gokmen,et al.  Beyond 11% Efficiency: Characteristics of State‐of‐the‐Art Cu2ZnSn(S,Se)4 Solar Cells , 2013 .

[7]  Tayfun Gokmen,et al.  Band tailing and efficiency limitation in kesterite solar cells , 2013 .

[8]  O. Gunawan,et al.  A parallel dipole line system , 2014, 1405.5220.

[9]  D. Mitzi,et al.  Semi-empirical device model for Cu2ZnSn(S,Se)4 solar cells , 2014 .

[10]  R. Agrawal,et al.  Optoelectronic and material properties of nanocrystal-based CZTSe absorbers with Ag-alloying , 2016 .

[11]  A. Walsh,et al.  Engineering Solar Cell Absorbers by Exploring the Band Alignment and Defect Disparity: The Case of Cu‐ and Ag‐Based Kesterite Compounds , 2015 .

[12]  Wei Wang,et al.  Electronic and elemental properties of the Cu2ZnSn(S,Se)4 surface and grain boundaries , 2014 .

[13]  Budhika G. Mendis,et al.  Direct observation of Cu, Zn cation disorder in Cu2ZnSnS4 solar cell absorber material using aberration corrected scanning transmission electron microscopy , 2014 .

[14]  Supratik Guha,et al.  Thin film solar cell with 8.4% power conversion efficiency using an earth‐abundant Cu2ZnSnS4 absorber , 2013 .

[15]  D. Mitzi,et al.  The Role of Sodium as a Surfactant and Suppressor of Non‐Radiative Recombination at Internal Surfaces in Cu2ZnSnS4 , 2015 .

[16]  Shujuan Huang,et al.  The role of Ag in (Ag,Cu)2ZnSnS4 thin film for solar cell application , 2015 .

[17]  A. Walsh,et al.  Intrinsic point defects and complexes in the quaternary kesterite semiconductor Cu2ZnSnS4 , 2010 .

[18]  M. Tovar,et al.  A neutron diffraction study of the stannite-kesterite solid solution series , 2007 .

[19]  A. Walsh,et al.  Classification of Lattice Defects in the Kesterite Cu2ZnSnS4 and Cu2ZnSnSe4 Earth‐Abundant Solar Cell Absorbers , 2013, Advanced materials.

[20]  G. Nolas,et al.  Synthesis and Characterization of Nanostructured Stannite Cu2ZnSnSe4 and Ag2ZnSnSe4 for Thermoelectric Applications. , 2015, ACS applied materials & interfaces.

[21]  Douglas M. Bishop,et al.  The impact of sodium on the sub-bandgap states in CZTSe and CZTS , 2015 .

[22]  C. Persson.  Electronic and optical properties of Cu2ZnSnS4 and Cu2ZnSnSe4 , 2010 .

[23]  Pekka Pyykkö,et al.  Molecular single-bond covalent radii for elements 1-118. , 2009, Chemistry.

[24]  O. Gunawan,et al.  Cu2ZnSnSe4 Thin‐Film Solar Cells by Thermal Co‐evaporation with 11.6% Efficiency and Improved Minority Carrier Diffusion Length , 2015 .

[25]  D. Mitzi,et al.  Electronic properties of the Cu2ZnSn(Se,S)4 absorber layer in solar cells as revealed by admittance spectroscopy and related methods , 2012 .

[26]  S. Siebentritt,et al.  What is the bandgap of kesterite , 2016 .