The effect of injection damage on a silicon bipolar low-noise amplifier

A study on the energy injection-induced damage, by a pulse-modulated RF signal source, to a silicon bipolar low-noise amplifier (LNA) is described in this paper based on the analysis of pre- and post-injection data of the noise figure and the gain. Experimental results show that both the noise and the gain characteristics of the LNA are sensitive to energy injection. Sample dissection analysis and simulation results also indicate that energy injection damages the base electrode, and thus causes the base resistor to increase, and, as a result, leads to an increase of the LNA noise. However, the gain of most LNA samples increases with the injection energy level following the time-based drift failure model of the bipolar current gain hFE. It is found that using the gain characteristics difference prior to and after the injection as the sole parameter to evaluate the damage is insufficient due to the complexity of the effect of energy injection-induced damage.

[1]  V. D. Dobykin,et al.  Electromagnetic-pulse functional damage of semiconductor devices modeled using temperature gradients as boundary conditions , 2006 .

[2]  Bruce Jacob,et al.  Electromagnetic Interference and Digital Circuits: An Initial Study of Clock Networks , 2006 .

[3]  Victor L. Granatstein,et al.  Effects of microwave interference on the operational parameters of n-channel enhancement mode MOSFET devices in CMOS integrated circuits , 2004 .

[4]  G. Masetti,et al.  Failures induced on analog integrated circuits by conveyed electromagnetic interferences: A review , 1996 .

[5]  Yiqi Zhuang,et al.  Correlation between 1/f noise and h/sub FE/ long-term instability in silicon bipolar devices , 1991 .

[6]  Scofield,et al.  Evidence that similar point defects cause 1/f noise and radiation-induced-hole trapping in metal-oxide-semiconductor transistors. , 1990, Physical review letters.

[7]  N. Bibić,et al.  Thermal diffusion in AuWTiPd metallization on silicon , 1990 .

[8]  Generation of interface states and oxide charges in n-MOS structures due to high electric field , 1989 .

[9]  Dali Mao,et al.  Interdiffusion of an Au/Ni/Cr multilayer metallization on silicon substrates , 1989 .

[10]  Ninoslav Stojadinovic,et al.  Analysis of CMOS transistor instabilities , 1987 .

[11]  H. Wong,et al.  Experimentally observed deviations from the superposition principle in crystalline silicon solar cells at low illuminations , 1987 .

[12]  B. Selikson,et al.  Void formation failure mechanisms in integrated circuits , 1969 .

[13]  George L. Schnable,et al.  Metalization and Bonds - A Review of Failure Mechanisms , 1967 .