Evaluation of plasma charging damage in ultrathin gate oxides

Monitoring of plasma charging damage in ultrathin oxides (e.g., <4 mm) is essential to understand its impact on device reliability. However, it is observed that the shift of several device parameters, including threshold voltage, transconductance, and subthreshold swing, are not sensitive to plasma charging and thus not suitable for this purpose. Consequently, some destructive methods, such as the charge-to-breakdown measurement, are necessary to evaluate plasma damage in the ultrathin oxides.

[1]  D. Wristers,et al.  Polarity dependence of dielectric breakdown in scaled SiO/sub 2/ , 1994, Proceedings of 1994 IEEE International Electron Devices Meeting.

[2]  J. McVittie,et al.  Plasma Charging Damage: An Overview , 1996, Proceedings of 1st International Symposium on Plasma Process-Induced Damage.

[3]  Horng-Chih Lin,et al.  Characterization of plasma charging damage in ultrathin gate oxides , 1998, 1998 IEEE International Reliability Physics Symposium Proceedings. 36th Annual (Cat. No.98CH36173).

[4]  Chenming Hu,et al.  Ultra-thin silicon dioxide leakage current and scaling limit , 1992, 1992 Symposium on VLSI Technology Digest of Technical Papers.

[5]  S.R. Nariani,et al.  A simple wafer-level measurement technique for predicting oxide reliability , 1995, IEEE Electron Device Letters.

[6]  James P. McVittie,et al.  Oxide damage from plasma charging: breakdown mechanism and oxide quality , 1994 .

[7]  K. Cheung,et al.  Plasma‐charging damage: A physical model , 1994 .

[8]  Horng-Chih Lin,et al.  Resist-related damage on ultrathin gate oxide during plasma ashing , 1997 .

[9]  J. McVittie,et al.  Modeling of oxide breakdown from gate charging during resist ashing , 1994 .

[10]  K. Cheung,et al.  Charging damage from plasma enhanced TEOS deposition , 1995, IEEE Electron Device Letters.