Characterisation and Reverse Engineering of Eco-friendly Historical Mortar: Qasr Tuba, Desert Castles in Jordan

The purpose of this study was to investigate the mineral composition of the historical mortars of Qasr Tuba and to re-produce them for the restoration process. The mortar samples were collected from the foundation and walls of Qasr Tuba. The chemical and mineral composition of the mortar was determined using several techniques. In addition, the quantitative minerals content was recalculated for the mortar samples utilizing the material balances equation. Moreover, 12 mixtures of mortar were prepared and tested for fresh and hardened properties, according to their respective national and international standards. The results revealed that two types of mortar were used: (i) the lime-based mortar was used for the foundation and joint mortars in the lower parts of the building walls with a gypsum-hydrated lime ratio of 1:3; and (ii) the gypsum-based mortar was used as joint mortar in the upper parts of the building walls for baked bricks at a gypsum-hydrated lime ratio of 4:1. A pozzolanic reaction in the Qasr Tuba mortar produced a new formation of Xonotlite, Stratlingite, and calcium aluminium hydrate as a secondary cementing mineral. In conclusion, the use of hydraulic lime mortar was considered for building an environment for capturing the CO2 gas.

[1]  Jan Válek,et al.  Recommendation of RILEM TC 243-SGM: functional requirements for surface repair mortars for historic buildings , 2019, Materials and Structures.

[2]  Alois Musil.  Arabia Petraea. I. Moab , 1907 .

[3]  M. Luxán,et al.  Ancient gypsum mortars from St. Engracia (Zaragoza, Spain): Characterization. Identification of additives and treatments , 1995 .

[4]  G. Chierici.  The Material Balance Equation , 1994 .

[5]  M. Murat.  Hydration reaction and hardening of calcined clays and related minerals. I. Preliminary investigation on metakaolinite , 1983 .

[6]  A. Aikin.  A manual of mineralogy , 1814 .

[7]  D. A. Elmeligy,et al.  Biomimicry For Ecologically Sustainable Design In Architecture: A Proposed Methodological Study , 2016, ARC 2016.

[8]  M. Murat.  Hydration reaction and hardening of calcined clays and related minerals , 1983 .

[9]  O. Henning.  Cements: the Hydrated Silicates and Aluminates , 1974 .

[10]  V. Weekman,et al.  Chemical Reaction Engineering , 1974 .

[11]  Carolyn L. Searls,et al.  Diagnosis of Terra-Cotta Glaze Spalling , 1988 .

[12]  David Dollimore,et al.  The kinetic interpretation of the decomposition of calcium carbonate by use of relationships other than the Arrhenius equation , 1996 .

[13]  H. Freund,et al.  Application of Fourier Transform Infrared Spectroscopy to Silica Diagenesis: The Opal-A to Opal-Ct Transformation , 1995 .

[14]  R. Ghirshman.  Iran : from the earliest times to the Islamic conquest , 1956 .

[15]  G. Rao,et al.  INVESTIGATIONS ON THE PERFORMANCE OF SILICA FUME-INCORPORATED CEMENT PASTES AND MORTARS , 2003 .

[16]  S. Martínez-Ramírez,et al.  Historic Mortars : Characterization and Durability . New Tendencies for Research , 2002 .

[17]  Luigia Binda,et al.  RILEM TC 203-RHM: Repair mortars for historic masonry , 2012, Materials and Structures.

[18]  Robert L. Lembright.  The Oxford History of Ancient Egypt , 2001 .

[19]  V. Farmer.  Atlas of Infrared Spectroscopy of Clay Minerals and their Admixtures , 1977 .

[20]  J. G. Cabrera,et al.  The effect of temperature on the hydration rate and stability of the hydration phases of metakaolin–lime–water systems , 2002 .