Determination of true stress corrosion cracking susceptibility index of a high strength Al alloy using glycerin as the non-corrosive atmosphere

[1]  V. S. Raja,et al.  Influence of Multistep Aging on the Stress Corrosion Cracking Behavior of Aluminum Alloy 7010 , 2003 .

[2]  R. Kelly,et al.  The Electrode Potential Dependence of Environment-Assisted Cracking of AA 7050 , 2000 .

[3]  L. Gan,et al.  Environment-Assisted Cracking of Al 2195 Alloy , 2000 .

[4]  S. Newcomb,et al.  The Influence of Microstructure on the Formation of Stress Corrosion Cracks in 7XXX Series Aluminium Alloys , 2000 .

[5]  M. O. Speidel,et al.  Stress corrosion cracking of two aluminium alloys: A comparison between experimental observations and data based on modelling , 1998 .

[6]  J. Damborenea,et al.  Characterization of the SCC behaviour of 8090 Al-Li alloy by means of the slow-strain-rate technique , 1998 .

[7]  T. Magnin,et al.  Influence of critical surface defects and localized competition between anodic dissolution and hydrogen effects during stress corrosion cracking of a 7050 aluminium alloy , 1997 .

[8]  B. Shaw,et al.  Technical Note: Stress Corrosion Cracking Behavior of Two High-Strength Al-xCu-Li-Ag-Mg-Zr Alloys , 1992 .

[9]  I. Bernstein,et al.  Microstructural effects on hydrogen embrittlement in a high purity 7075 aluminum alloy , 1987 .

[10]  V. M. Polyanskii.  Role of hydrogen embrittlement in the corrosion cracking of aluminum alloys , 1986 .

[11]  S. Lynch.  Mechanisms of environmentally assisted cracking in AlZnMg single crystals , 1982 .

[12]  N. Holroyd,et al.  Strain-rate effects in the environmentally assisted fracture of a commercial high-strength aluminium alloy (7049) , 1981 .

[13]  R. N. Parkins,et al.  Reduced ductility of high-strength aluminium alloy during or after exposure to water , 1979 .

[14]  P. Swann,et al.  Pre-exposure embrittlement and stress corrosion failure in AlZnMg Alloys , 1976 .

[15]  M. O. Speidel,et al.  Stress corrosion cracking of aluminum alloys , 1975 .

[16]  J. Scully,et al.  The effect of atmospheric moisture upon the S.C.C. of an Al−6Zn−3Mg alloy , 1971 .