Injection molding of products with functional surfaces by micro-structured, PVD coated injection molds

Molding of micro structures by injection molding leads to special requirements for the molds e.g. regarding wear resistance and low release forces of the molded components. At the same time it is not allowed to affect the replication precision. Physical vapor deposition (PVD) is one of the promising technologies for applying coatings with adapted properties like high hardness, low roughness, low Young’s modulus and less adhesion to the melt of polymers. Physical vapor deposition technology allows the deposition of thin films on micro structures. Therefore, the influence of these PVD layers on the contour accuracy of the replicated micro structures has to be investigated. For this purpose injection mold inserts were laser structured with micro structures of different sizes and afterwards coated with two different coatings, which were deposited by a magnetron sputter ion plating PVD technology. After deposition, the coatings were analyzed by techniques regarding hardness, Young’s modulus and morphology. The geometries of the micro structures were analyzed by scanning electron microscopy before and after coating. Afterwards, the coated mold inserts were used for injection molding experiments. During the injection molding process, a conventional and a variothermal temperature control of the molds were used. The molded parts were analyzed regarding roughness, structure height and structure width by means of laser microscopy.

[1]  Christina Berger,et al.  Datensammlung zu Hartstoffeigenschaften , 1997 .

[2]  Investigations in Injection Moulding of Micro Structures and Microstructured Surfaces , 2007 .

[3]  E. Lugscheider,et al.  (Cr1‐x,Alx)N ein Review über ein vielseitig einsetzbares Schichtsystem , 2006 .

[4]  A. Tünnermann,et al.  Femtosecond, picosecond and nanosecond laser ablation of solids , 1996 .

[5]  M. Heinze.  Wear resistance of hard coatings in plastics processing , 1998 .

[6]  Friedrich Dausinger,et al.  Surface structuring of metals with ultrashort laser pulses , 2003 .

[7]  Masahito Katto,et al.  Microstructures formation on titanium plate by femtosecond laser ablation , 2007 .

[8]  Jung-Joong Lee,et al.  Compositionally gradient (Ti1−xAlx)N coatings made by plasma enhanced chemical vapor deposition , 1995 .

[9]  Nazlim Bagcivan,et al.  PVD—Coatings in Injection Molding Machines for Processing Optical Polymers , 2007 .

[10]  A. Cunha,et al.  Performance of chromium nitride and titanium nitride coatings during plastic injection moulding , 2002 .

[11]  Boris N. Chichkov,et al.  Ablation of metals by ultrashort laser pulses , 1997 .

[12]  C. Hartmann,et al.  Investigation on laser micro ablation of steel using PS-IR pulse bursts , 2007 .

[13]  G. Botton,et al.  Crystalline orientation effects on conical structure formation in femtosecond laser irradiation of silicon and germanium , 2010 .

[14]  G. Pharr,et al.  An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments , 1992 .

[15]  N. Huang,et al.  Comparison of tribological behaviours of AlCrN and TiAlN coatings—Deposited by physical vapor deposition , 2007 .

[16]  S. Nikumb,et al.  Femtosecond laser micromilling of Si wafers , 2008 .

[17]  Yunmei Fang,et al.  Wear progressions and tool life enhancement with AlCrN coated inserts in high-speed dry and wet steel lathing , 2008 .