Determination of the oxygen and nitrogen interstitial diffusion coeficient in niobium by mechanical spectroscopy

Mechanical spectroscopy measurements have been extensively used in the last decades to obtain information about many aspects of the behavior of solutes in metallic materials. Metals of body-centered cubic lattice that contain heavy interstitial elements (oxygen, nitrogen and carbon) in solid solution, present anelastic relaxation peaks when submitted to cyclic tensions, due to process know stress-induced ordering. Internal friction and frequency as a function of temperature were performed between 300 K and 650 K in a polycrystalline sample of Nb, for three distinct conditions, using a torsion pendulum inverted Ke-type operating in a frequency oscillation between 1Hz and 10 Hz range, with a heating rate of 1 K/min and pressure lower than 2 x 10-5 mbar. The experimental spectra obtained for each condition of the sample, were decomposed by the successive subtraction method in elementary Debye peaks. The following metal-interstitial interactions were identified: Nb-O and Nb-N for all conditions of the sample. From the anelastic relaxation parameters obtained (relaxation strength, peak temperature, activation energy and relaxation time) and lattice parameter (obtained from x ray diffraction), the determination of the oxygen and nitrogen interstitial diffusion coefficient in Nb was possible, for each condition of the sample.