Facile synthesis of rutile TiO2 nanorod microspheres for enhancing light-harvesting of dye-sensitized solar cells

Sub-micrometer sized rutile TiO2 nanorod microspheres with diameters of 500–700 nm and with a specific surface area of 63.7 m2 g−1 were synthesized via a salt-assisted hydrothermal method. Morphological evolution as a function of reaction time was carried out to gain insight into the formation mechanism of the nanorod microspheres. Unlike traditional bulk rutile TiO2 particles, the nanorod microspheres could provide dual-functions of adsorbing dye molecules and strong light-harvesting efficiency when they were fabricated as a scattering overlayer in dye-sensitized solar cells (DSSCs). Furthermore, the inherent nanorods would provide excellent electron percolation pathways for charge transfer as confirmed by electrochemical impedance spectroscopy. Consequentially, DSSC with the scattering overlayer exhibited a 39% increment of cell efficiency (7.32%) compared with the DSSC without one (5.28%), and the efficiency was also a little higher than the DSSC with the same thickness composed of only nanocrystallites (7.14%).

[1]  Qing Wang,et al.  Characteristics of high efficiency dye-sensitized solar cells. , 2006, The journal of physical chemistry. B.

[2]  Nam-Gyu Park,et al.  Compact Inverse‐Opal Electrode Using Non‐Aggregated TiO2 Nanoparticles for Dye‐Sensitized Solar Cells , 2009 .

[3]  Wenming Tong,et al.  Supersaturated spontaneous nucleation to TiO2 microspheres: synthesis and giant dielectric performance. , 2010, Chemical communications.

[4]  Hua Wang,et al.  SnO2 hollow nanospheres enclosed by single crystalline nanoparticles for highly efficient dye-sensitized solar cells , 2012 .

[5]  Nam-Gyu Park,et al.  Nano‐embossed Hollow Spherical TiO2 as Bifunctional Material for High‐Efficiency Dye‐Sensitized Solar Cells , 2008 .

[6]  Shih‐Yuan Lu,et al.  A novel way of improving light harvesting in dye-sensitized solar cells – Electrodeposition of titania , 2009 .

[7]  Qing Zhang and,et al.  Preparation of oxide nanocrystals with tunable morphologies by the moderate hydrothermal method: Insights from rutile TiO2 , 2003 .

[8]  Shengyuan Yang,et al.  Which is a superior material for scattering layer in dye-sensitized solar cells—electrospun rice grain- or nanofiber-shaped TiO2? , 2011 .

[9]  Fuzhi Huang,et al.  Dual‐Function Scattering Layer of Submicrometer‐Sized Mesoporous TiO2 Beads for High‐Efficiency Dye‐Sensitized Solar Cells , 2010 .

[10]  Michael Grätzel,et al.  Porphyrin-Sensitized Solar Cells with Cobalt (II/III)–Based Redox Electrolyte Exceed 12 Percent Efficiency , 2011, Science.

[11]  Dong‐Wan Kim,et al.  Enhancement of cyclability of urchin-like rutile TiO2 submicron spheres by nanopainting with carbon , 2012 .

[12]  Xiaopeng Zhao,et al.  Well-organized 3D urchin-like hierarchical TiO2 microspheres with high photocatalytic activity , 2012, Journal of Materials Science.

[13]  Shuhong Yu,et al.  Recent advances in oriented attachment growth and synthesis of functional materials: concept, evidence, mechanism, and future , 2009 .

[14]  Jianfeng Chen,et al.  Dual-functional ZnO nanorod aggregates as scattering layer in the photoanode for dye-sensitized solar cells. , 2011, Chemical communications.

[15]  R. Vittal,et al.  CTAB facilitated spherical rutile TiO2 particles and their advantage in a dye-sensitized solar cell , 2008 .

[16]  Yangxuan Xiao,et al.  TiO2‐Coated Multilayered SnO2 Hollow Microspheres for Dye‐Sensitized Solar Cells , 2009 .

[17]  M. Grätzel,et al.  A low-cost, high-efficiency solar cell based on dye-sensitized colloidal TiO2 films , 1991, Nature.

[18]  P. Liska,et al.  Fabrication of thin film dye sensitized solar cells with solar to electric power conversion efficiency over 10 , 2008 .

[19]  Sarmimala Hore,et al.  Scattering spherical voids in nanocrystalline TiO2- enhancement of efficiency in dye-sensitized solar cells. , 2005, Chemical communications.

[20]  Bin Liu,et al.  Growth of oriented single-crystalline rutile TiO(2) nanorods on transparent conducting substrates for dye-sensitized solar cells. , 2009, Journal of the American Chemical Society.

[21]  Chongmu Lee,et al.  Size-dependent light-scattering effects of nanoporous TiO2 spheres in dye-sensitized solar cells , 2011 .

[22]  H. Smit,et al.  Influence of scattering layers on efficiency of dye-sensitized solar cells , 2006 .

[23]  H. M. Jang,et al.  Size-tunable mesoporous spherical TiO2 as a scattering overlayer in high-performance dye-sensitized solar cells , 2011 .

[24]  D. Kuang,et al.  Tri-functional hierarchical TiO2 spheres consisting of anatase nanorods and nanoparticles for high efficiency dye-sensitized solar cells , 2011 .

[25]  Yongcai Qiu,et al.  Double-layered photoanodes from variable-size anatase TiO2 nanospindles: a candidate for high-efficiency dye-sensitized solar cells. , 2010, Angewandte Chemie.

[26]  R. Vittal,et al.  TiO2 nanorods as additive to TiO2 film for improvement in the performance of dye-sensitized solar cells , 2006 .

[27]  Z. Tang,et al.  Facile synthesis of Au@TiO2 core–shell hollow spheres for dye-sensitized solar cells with remarkably improved efficiency , 2012 .

[28]  Joachim Luther,et al.  Modeling and interpretation of electrical impedance spectra of dye solar cells operated under open-circuit conditions , 2002 .

[29]  G. Lu,et al.  Shell-in-shell TiO2 hollow spheres synthesized by one-pot hydrothermal method for dye-sensitized solar cell application , 2011 .