Enhancement in Thermoelectric Figure‐Of‐Merit of an N‐Type Half‐Heusler Compound by the Nanocomposite Approach

An enhancement in the dimensionless thermoelectric figure‐of‐merit (ZT) of an n‐type half‐Heusler material is reported using a nanocomposite approach. A peak ZT value of 1.0 was achieved at 600 °C–700 °C, which is about 25% higher than the previously reported highest value. The samples were made by ball‐milling ingots of composition Hf0.75Zr0.25NiSn0.99Sb0.01 into nanopowders and hot‐pressing the powders into dense bulk samples. The ingots were formed by arc‐melting the elements. The ZT enhancement mainly comes from reduction of thermal conductivity due to increased phonon scattering at grain boundaries and crystal defects, and optimization of antimony doping.

[1]  Joseph Callaway,et al.  Effect of Point Imperfections on Lattice Thermal Conductivity , 1960 .

[2]  Cronin B. Vining,et al.  Thermoelectric properties of pressure-sintered Si0.8Ge0.2 thermoelectric alloys , 1991 .

[3]  D. Rowe,et al.  Comments on the thermoelectric properties of pressure‐sintered Si0.8Ge0.2 thermoelectric alloys , 1993 .

[4]  Band gap and stability in the ternary intermetallic compounds NiSnM (M=Ti,Zr,Hf): A first-principles study. , 1994, Physical review. B, Condensed matter.

[5]  D. Rowe.  CRC Handbook of Thermoelectrics , 1995 .

[6]  R. K. Williams,et al.  Filled Skutterudite Antimonides: A New Class of Thermoelectric Materials , 1996, Science.

[7]  M. A. Kouacou,et al.  Crossover from semiconductor to magnetic metal in semi-Heusler phases as a function of valence electron concentration , 1998 .

[8]  J. Toboła,et al.  Electronic phase diagram of the XTZ (X=Fe, Co, Ni; T=Ti, V, Zr, Nb, Mn; Z=Sn, Sb) semi-Heusler compounds , 2000 .

[9]  M. Kanatzidis,et al.  Structural stability of Ni-containing half-Heusler compounds , 2000 .

[10]  S. Poon,et al.  Thermoelectric properties of semimetallic (Zr, Hf)CoSb half-Heusler phases , 2000 .

[11]  Terry M. Tritt,et al.  Recent trends in thermoelectric materials research , 2001 .

[12]  G. Poon,et al.  Chapter 2 Electronic and thermoelectric properties of Half-Heusler alloys , 2001 .

[13]  Qiang Shen,et al.  Effects of partial substitution of Ni by Pd on the thermoelectric properties of ZrNiSn-based half-Heusler compounds , 2001 .

[14]  I. Dasgupta,et al.  Electronic structure and magnetism in half-Heusler compounds , 2003 .

[15]  M. Kanatzidis,et al.  Cubic AgPbmSbTe2+m: Bulk Thermoelectric Materials with High Figure of Merit , 2004, Science.

[16]  G. Meisner,et al.  Strain field fluctuation effects on lattice thermal conductivity of ZrNiSn-based thermoelectric compounds , 2004 .

[17]  Y. Isoda,et al.  Temperature dependence of thermoelectric properties of Ni-doped CoSb3 , 2005 .

[18]  Terry M. Tritt,et al.  Effect of substitutions on the thermoelectric figure of merit of half-Heusler phases at 800 °C , 2006 .

[19]  Y. Kimura,et al.  Thermoelectric properties of p-type half-Heusler compound HfPtSn and improvement for high-performance by Ir and Co additions , 2006 .

[20]  Xiangyang Huang,et al.  The high temperature thermoelectric performances of Zr0.5Hf0.5Ni0.8Pd0.2Sn0.99Sb0.01 alloy with nanophase inclusions , 2006 .

[21]  Jingfeng Li,et al.  Enhanced thermoelectric properties in CoSb3-xTex alloys prepared by mechanical alloying and spark plasma sintering , 2007 .

[22]  Lidong Chen,et al.  Thermoelectric properties of p-type Fe-doped TiCoSb half-Heusler compounds , 2007 .

[23]  M. Dresselhaus,et al.  New Directions for Low‐Dimensional Thermoelectric Materials , 2007 .

[24]  Hohyun Lee,et al.  Enhanced thermoelectric figure-of-merit in nanostructured p-type silicon germanium bulk alloys. , 2008, Nano letters.

[25]  C. Uher,et al.  Low thermal conductivity and high thermoelectric figure of merit in n-type BaxYbyCo4Sb12 double-filled skutterudites , 2008 .

[26]  Hohyun Lee,et al.  Enhanced thermoelectric figure of merit in nanostructured n-type silicon germanium bulk alloy , 2008 .

[27]  G. J. Snyder,et al.  Enhancement of Thermoelectric Efficiency in PbTe by Distortion of the Electronic Density of States , 2008, Science.

[28]  M. Dresselhaus,et al.  High-Thermoelectric Performance of Nanostructured Bismuth Antimony Telluride Bulk Alloys , 2008, Science.

[29]  S. Poon,et al.  (Zr,Hf)Co(Sb,Sn) half-Heusler phases as high-temperature (>700°C) p-type thermoelectric materials , 2008 .

[30]  Jihui Yang,et al.  Solubility study of Yb in n-type skutterudites YbxCo4Sb12 and their enhanced thermoelectric properties , 2009 .

[31]  Terry M. Tritt,et al.  High thermoelectric performance BiSbTe alloy with unique low-dimensional structure , 2009 .

[32]  M. Hvistendahl.  Social science. Survey to reveal true face of Chinese society. , 2010, Science.

[33]  Gang Chen,et al.  Enhanced thermoelectric figure of merit of p-type half-Heuslers. , 2011, Nano letters.