A thin film nitinol heart valve.

In order to create a less thrombogenic heart valve with improved longevity, a prosthetic heart valve was developed using thin film nitinol (NiTi). A "butterfly" valve was constructed using a single, elliptical piece of thin film NiTi and a scaffold made from Teflon tubing and NiTi wire. Flow tests and pressure readings across the valve were performed in vitro in a pulsatile flow loop. Bio-corrosion experiments were conducted on untreated and passivated thin film nitinol. To determine the material's in vivo biocompatibility, thin film nitinol was implanted in pigs using stents covered with thin film NiTi. Flow rates and pressure tracings across the valve were comparable to those through a commercially available 19 mm Perimount Edwards tissue valve. No signs of corrosion were present on thin film nitinol samples after immersion in Hank's solution for one month. Finally, organ and tissue samples explanted from four pigs at 2, 3, 4, and 6 weeks after thin film NiTi implantation appeared without disease, and the thin film nitinol itself was without thrombus formation. Although long term testing is still necessary, thin film NiTi may be very well suited for use in artificial heart valves.

[1]  Assaf Bash,et al.  Percutaneous Transcatheter Implantation of an Aortic Valve Prosthesis for Calcific Aortic Stenosis: First Human Case Description , 2002, Circulation.

[2]  C. Claussen,et al.  Thrombogenicity of various endovascular stent types: an in vitro evaluation. , 2002, Journal of vascular and interventional radiology : JVIR.

[3]  Younes Boudjemline,et al.  Percutaneous insertion of the pulmonary valve. , 2002, Journal of the American College of Cardiology.

[4]  B. O'brien,et al.  Passivation of nitinol wire for vascular implants--a demonstration of the benefits. , 2002, Biomaterials.

[5]  Younes Boudjemline,et al.  Steps Toward Percutaneous Aortic Valve Replacement , 2002, Circulation.

[6]  H Bergmann,et al.  In-vitro assessment of a registration protocol for image guided implant dentistry. , 2001, Clinical oral implants research.

[7]  A. Pelton,et al.  An overview of nitinol medical applications , 1999 .

[8]  F J Schoen,et al.  Founder's Award, 25th Annual Meeting of the Society for Biomaterials, perspectives. Providence, RI, April 28-May 2, 1999. Tissue heart valves: current challenges and future research perspectives. , 1999, Journal of biomedical materials research.

[9]  T. Lehnert,et al.  A new fabrication process for Ni–Ti shape memory thin films , 1999 .

[10]  L. Yahia,et al.  Effect of modification of oxide layer on NiTi stent corrosion resistance. , 1998, Journal of biomedical materials research.

[11]  Takayuki Shibata,et al.  Flash evaporation of TiNi shape memory thin film for microactuators , 1998 .

[12]  Don P. Giddens,et al.  Chapter 16 Prosthetic Cardiac Valves , 1993 .

[13]  S. Shabalovskaya,et al.  Surface, corrosion and biocompatibility aspects of Nitinol as an implant material. , 2002, Bio-medical materials and engineering.

[14]  R. W. Fox,et al.  Prosthetic cardiac valves. An in vitro study. , 1972 .