Measuring Strains for Hematite Phase in Sinter Ore by Electron Backscattering Diffraction Method

Based on the relationship between quantified blurring degree of Kikuchi bands obtained by an electron backscattering diffraction (EBSD) technique and macroscopic strains measured by a strain gauge, the local compression strain SEBSD in sinter ore has been evaluated under various conditions. There is a good linear relationship between the SEBSD and the strains measured by a strain gauge. The local strain SEBSD evaluated by EBSD patterns can be used as an index of local strains.

[1] A. Wilkinson,et al. Quantitative deformation studies using electron back scatter patterns , 1991 .

[2] M. Shimizu,et al. Mechanism of the Non-uniform Sintering on Using a Low-Al2O3 Pisolite Ore , 1996 .

[3] N. Taguchi,et al. Suppression of the Formation of Large Pores in the Assimilated Parts of Sinter Produced Using Pisolitic Ores , 1996 .

[4] K. Kunze,et al. Orientation imaging: The emergence of a new microscopy , 1993 .

[5] D. Dingley,et al. Backscatter Kikuchi diffraction in the SEM for identification of crystallographic point groups , 1989 .

[6] L. Yang,et al. Introduction of Pisolitic Goethite Ore into a Chinese Ore Blend , 2000 .

[7] P. J. Henderson,et al. Observations of deformation and fracture heterogeneities in a nickel-base superalloy using electron back scattering patterns , 1988 .