Effect of Fly Ash on the Durability Properties of High Strength Concrete

Abstract Utilization of fly ash as a supplementary cementitious material adds sustainability to concrete by reducing the CO2 emission of cement production. The positive effects of fly ash as a partial replacement of cement on the durability of concrete are recognized through numerous researches; however, the extent of improvement depends on the properties of fly ash. In this study, durability properties of high strength concrete utilizing high volume Class F fly ash sourced from Western Australia have been investigated. Concrete mixtures with fly ash as 30% and 40% of total binder were used to cast the test specimens. The compressive strength, drying shrinkage, sorptivity and rapid chloride permeability of the fly ash and control concrete specimens were determined. The 28-day compressive strength of the concrete mixtures varied from 65 to 85 MPa. The fly ash concrete samples showed less drying shrinkage than the control concrete samples when designed for the same 28-day compressive strength of the control concrete. Inclusion of fly ash reduced sorptivity and chloride ion permeation significantly at 28 days and reduced further at 6 months. In general, incorporation of fly ash as partial replacement of cement improved the durability properties of concrete.

[1]  V. Papadakis.  Effect of fly ash on Portland cement systems. Part II. High-calcium fly ash , 1999 .

[2]  C. Tasdemir,et al.  Combined effects of mineral admixtures and curing conditions on the sorptivity coefficient of concrete , 2003 .

[3]  V. Malhotra,et al.  MECHANICAL PROPERTIES OF CONCRETE INCORPORATING HIGH VOLUMES OF FLY ASH FROM SOURCES IN THE U.S. , 1993 .

[4]  T. Naik,et al.  Permeability of concrete containing large amounts of fly ash , 1994 .

[5]  V. Sirivivatnanon,et al.  Influence of fly ash fineness on strength, drying shrinkage and sulfate resistance of blended cement mortar , 2004 .

[6]  V. Malhotra.  Durability of concrete incorporating high-volume of low-calcium (ASTM Class F) fly ash , 1990 .

[7]  Rafat Siddique,et al.  Performance characteristics of high-volume Class F fly ash concrete , 2004 .

[8]  Gary Knight,et al.  Guide for Selecting Proportions for High-Strength Concrete Using Portland Cement and Other Cementitious Materials , 2008 .

[9]  F Papworth,et al.  Designing for Concrete Durability in Marine Environs , 1985 .

[10]  Vagelis G. Papadakis,et al.  Effect of fly ash on Portland cement systems , 1999 .

[11]  V. M. Malhotra,et al.  Introduction: Sustainable Development and Concrete Technology , 2002 .

[12]  J. L. Barroso de Aguiar,et al.  Durability of Low Cost High Performance Fly Ash Concrete , 2003 .

[13]  P. Bowen,et al.  Changes in portlandite morphology with solvent composition: Atomistic simulations and experiment , 2011 .

[14]  C. Atiş.  High-Volume Fly Ash Concrete with High Strength and Low Drying Shrinkage , 2003 .

[15]  R. C. Joshi,et al.  Reexamination of ASTM C 1202 : Standard test method for electrical indication of concrete's ability to resist chloride ion penetration , 2000 .

[16]  V. Malhotra,et al.  Structural Concrete Incorporating High Volumes of ASTM Class Fly Ash , 1989 .