Local field emission from individual vertical carbon nanofibers grown on tungsten filament

Individual high-aspect-ratio carbon nanofibers (CNFs) were grown on tungsten filament substrates by plasma-enhanced hot filament chemical vapor deposition. They are similar to100 nm in diameter and 6-30 mum in length with a density less than 106/cm(2). The field emission property of single as-grown carbon nanofibers was measured in a scanning electron microscope equipped with a moveable nanoscale probe tip. The measurement results showed that the threshold field of single carbon nanofibers with different lengths was in the range of 4-5 V/mum with a corresponding emission current density of 20 muA/cm(2), but an evident difference in the enhancement of emitted current between nanofibers of different lengths could be found when the applied field was increased continuously. This indicates that the field emission property of single carbon nanofibers depends mainly upon their length, which is essentially attributed to the change of field enhancement factor of single carbon nanofibers. In addition, field emission of the different positions on the wall of a single carbon nanofiber was studied. (C) 2004 Elsevier Ltd. All rights reserved.

[1]  Robert P. H. Chang,et al.  A nanotube-based field-emission flat panel display , 1998 .

[2]  Christian Klinke,et al.  Field emission of individual carbon nanotubes in the scanning electron microscope. , 2002, Physical review letters.

[3]  Gehan A. J. Amaratunga,et al.  Field emission from dense, sparse and patterned arrays of carbon nanofibers , 2002 .

[4]  Vladimir I. Merkulov,et al.  Patterned growth of individual and multiple vertically aligned carbon nanofibers , 2000 .

[5]  W. D. de Heer,et al.  Nanomechanics of individual carbon nanotubes from pyrolytically grown arrays. , 2000, Physical review letters.

[6]  W. D. de Heer,et al.  A Carbon Nanotube Field-Emission Electron Source , 1995, Science.

[7]  S. H. Jo,et al.  Effect of length and spacing of vertically aligned carbon nanotubes on field emission properties , 2003 .

[8]  Gehan A. J. Amaratunga,et al.  Field electron emission from individual carbon nanotubes of a vertically aligned array , 2002 .

[9]  B. Chalamala,et al.  Current saturation mechanisms in carbon nanotube field emitters , 2000 .

[10]  Thomas Stöckli,et al.  Field emission from carbon nanotubes: the first five years , 2001 .

[11]  László Forró,et al.  Field emission from single-wall carbon nanotube films , 1998 .

[12]  Philip G. Collins,et al.  UNIQUE CHARACTERISTICS OF COLD CATHODE CARBON-NANOTUBE-MATRIX FIELD EMITTERS , 1997 .

[13]  Yahachi Saito,et al.  Cathode Ray Tube Lighting Elements with Carbon Nanotube Field Emitters , 1998 .

[14]  Yan Chen,et al.  Field emission from aligned high-density graphitic nanofibers , 1998 .

[15]  L. Schlapbach,et al.  Electron field emission from phase pure nanotube films grown in a methane/hydrogen plasma , 1998 .

[16]  E. W. Plummer,et al.  Field Emission Energy Distribution (FEED) , 1973 .

[17]  U. Valdré,et al.  Experimental and computational study of field emission characteristics from amorphous carbon single nanotips grown by carbon contamination. I. Experiments and computation , 2002 .

[18]  Robert P. H. Chang,et al.  Field emission from nanotube bundle emitters at low fields , 1997 .

[19]  P. Nordlander,et al.  Unraveling Nanotubes: Field Emission from an Atomic Wire , 1995, Science.