Synthesis and Characterization of NanocrystallineMg-7.4%Al Powders Produced by Mechanical Alloying

Nanocrystalline Mg-7.4%Al powder was prepared by mechanical alloying using a high-energy mill. The evolution of the various phases and their microstructure, including size and morphology of the powder particles in the course of milling and during subsequent annealing, were investigated in detail. Room temperature milling leads to a rather heterogeneous microstructure consisting of two distinct regions: Al-free Mg cores and Mg-Al intermixed areas. As a result, the material is mechanically heterogeneous with the Mg cores displaying low hardness (40–50 HV) and the Mg-Al intermixed regions showing high hardness of about 170 HV. The Mg cores disappear and the microstructure becomes (also mechanically) homogeneous after subsequent cryo-milling. Rietveld structure refinement reveals that the crystallite size of the milled powders decreases with increasing the milling time reaching a minimum value of about 30 nm. This is corroborated by transmission electron microscopy confirming an average grain size of ~25 nm.

[1]  C. Koch,et al.  High hardness in a nanocrystalline Mg97Y2Zn1 alloy , 2011 .

[2]  J. Bell,et al.  Compressive behaviour of nanocrystallilne Mg-5%Al alloys , 2010 .

[3]  J. Eckert,et al.  Mechanical alloying and milling of Al–Mg alloys , 2009 .

[4]  R. Scattergood,et al.  Grain-size stabilization in nanocrystalline FeZr alloys , 2008 .

[5]  A. Mallick.  Nanocrystalline Mg-3%Al Alloy: its Synthesis and Investigation of its Tensile Behavior , 2008 .

[6]  J. Eckert,et al.  Conditions for quasicrystal formation from mechanically alloyed Zr-based glassy powders , 2007 .

[7]  L. Anand,et al.  A constitutive model for powder-processed nanocrystalline metals , 2007 .

[8]  C. Koch.  Mechanical Milling and Alloying , 2006 .

[9]  Li Lu,et al.  Deformation behaviour of ultrafine and nanosize-grained Mg alloy synthesized via mechanical alloying , 2006 .

[10]  K. Kurzydłowski,et al.  Thermal Stability of Nanocrystalline Ni , 2002 .

[11]  C. Koch,et al.  Nanostructured Materials: Processing Properties, and Potential Applications , 2002 .

[12]  T. Roisnel,et al.  WinPLOTR: A Windows Tool for Powder Diffraction Pattern Analysis , 2001 .

[13]  B. Mordike,et al.  Magnesium: Properties — applications — potential , 2001 .

[14]  Li Lu,et al.  Influence of process control agent on interdiffusion between Al and Mg during mechanical alloying , 1999 .

[15]  U. Klement,et al.  Thermal stability of nanocrystalline Ni , 1995 .

[16]  A. Al-Azzawi,et al.  Mechanical Alloying and Milling , 2015 .

[17]  S. Scudino,et al.  Solid-state processing of Al-Mg alloys , 2009 .

[18]  C. Koch,et al.  Processing-structure-property relationships in ultrafine grain and nanocrystalline materials , 2009 .

[19]  L. Ye,et al.  Nanostructured High Strength Mg-5%Al-X%Nd Alloys Prepared by Mechanical Alloying , 2004 .

[20]  J. Eckert,et al.  Mechanically alloyed glassy metals , 1994 .

[21]  W. Johnson,et al.  Thermal stability and grain growth behavior of mechanically alloyed nanocrystalline Fe-Cu alloys , 1993 .