Densification and Mechanical Properties of Spark Plasma Sintered B4C with Si as a Sintering Aid

B 4 C ceramics doped with different Si contents were fabricated by the spark plasma sintering technique. Pure B 4 C ceramic could be densified to 99% of the theoretical density. The sinterability could be further improved by the addition of a small amount of Si due to the formation of liquid Si during sintering. The incorporation of Si could also remarkably increase the mechanical properties of B 4 C ceramics. The Vickers hardness, flexural strength, and fracture toughness of the sample with 8 wt% Si could reach 41.8 GPa, 640 MPa, and 6.1 MPa. m 1/2 . The improvement in hardness and strength was attributed to grain refinement. Crack deflection due to the thermal expansion mismatch between the B 4 C and SiC was found to be the main toughening mechanism.

[1]  M. Nygren,et al.  Densification and Mechanical Behavior of HfC and HfB2 Fabricated by Spark Plasma Sintering , 2008 .

[2]  N. Frage,et al.  The morphology of ceramic phases in BxC–SiC–Si infiltrated composites , 2006 .

[3]  Jingxian Zhang,et al.  Synthesis of silicon nitride-barium aluminosilicate self-reinforced ceramic composite by a two-step pressureless sintering , 2005 .

[4]  J. Zorzi,et al.  Hardness and wear resistance of B4C ceramics prepared with several additives , 2005 .

[5]  A. Mukherjee,et al.  Spark plasma sintering of silicon nitride/silicon carbide nanocomposites with reduced additive amounts , 2005 .

[6]  M. Esfandeh,et al.  Copper injection molding using a thermoplastic binder based on paraffin wax , 2005 .

[7]  Hyoun‐Ee Kim,et al.  Densification and Mechanical Properties of B4C with Al2O3 as a Sintering Aid , 2004 .

[8]  R. Speyer,et al.  Pressureless Sintering of Boron Carbide , 2003 .

[9]  C. Liu.  Structure and properties of boron carbide with aluminum incorporation , 2000 .

[10]  J. Petrovic,et al.  Ductile phase toughening and R-curve behaviour in a B4C-Al cermet , 1992 .

[11]  Brian R. Lawn,et al.  A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness: I , 1981 .

[12]  B. Champagne,et al.  Mechanical Properties of Hot‐Pressed B‐B4C Materials , 1979 .

[13]  M. Uehara,et al.  SiC–B4C composites for synergistic enhancement of thermoelectric property , 2004 .

[14]  M. Nygren,et al.  Kinetic aspects of superfast consolidation of silicon nitride based ceramics by spark plasma sintering , 2001 .

[15]  L. Sigl.  Processing and mechanical properties of boron carbide sintered with TiC , 1998 .

[16]  Z. Lihua,et al.  Structure of C-B4C-SiC composites with silicon additive , 1996 .

[17]  R. Telle,et al.  Reactive formation of coatings at boron carbide interface with Ti and Cr powders , 1995 .

[18]  F. Thévenot,et al.  Boron carbide ― a comprehensive review , 1990 .

[19]  D. K. Kim,et al.  Pressureless sintering and microstructural development of B sub 4 C-TiB sub 2 composites , 1988 .