Mechanical Properties and Morphology of Polylactide Composites with Acrylic Impact Modifier

Polylactide (PLA) composites with acrylic impact modifier BPM, i.e., PLA/BPM composites, were produced by the melt blending method. The effects of BPM on the thermal properties, melting behaviors, and dynamic mechanical properties of the PLA/BPMs were investigated by thermogravimetric analysis, differential scanning calorimetry, and dynamic mechanical analysis. Tensile strength, flexural strength, and modulus of the injection molded specimens were measured by an Instron tensile machine. The influence of BPM on the impact strength of injection molded PLA/BPM composites was examined using an impact tester. The morphology of cryofractured surfaces and fracture surfaces of the composites after the tensile and impact testing was also investigated using scanning electron microscope. The test results show that the composites with BPM possess better flexibility when compared with neat PLA. However, the notched Izod impact strength showed improvement only when the BPM content was higher than 15 wt%.

[1]  A. Herrmann,et al.  Natural and man-made cellulose fibre-reinforced poly(lactic acid) (PLA) composites: An overview about mechanical characteristics and application areas , 2009 .

[2]  H. Yano,et al.  The effect of crystallization of PLA on the thermal and mechanical properties of microfibrillated cellulose-reinforced PLA composites , 2009 .

[3]  A. N. Nakagaito,et al.  Production of microfibrillated cellulose (MFC)-reinforced polylactic acid (PLA) nanocomposites from sheets obtained by a papermaking-like process , 2009 .

[4]  E. Thostenson,et al.  Multi-scale hybrid biocomposite: Processing and mechanical characterization of bamboo fiber reinforced PLA with microfibrillated cellulose , 2009 .

[5]  Qinglin Wu,et al.  Modeling diameter distributions of poly( N -isopropylacrylamide- co -methacrylic acid) nan , 2009 .

[6]  N. Graupner.  Improvement of the Mechanical Properties of Biodegradable Hemp Fiber Reinforced Poly(lactic acid) (PLA) Composites by the Admixture of Man-made Cellulose Fibers , 2009 .

[7]  E. Piorkowska,et al.  Mechanical and thermal properties of green polylactide composites with natural fillers. , 2008, Macromolecular bioscience.

[8]  P. Dubois,et al.  Polylactide (PLA) and Highly Filled PLA ‐ Calcium Sulfate Composites with Improved Impact Properties , 2008 .

[9]  Linbo Wu,et al.  Poly(L-Lactic Acid)/Silicon Dioxide Nanocomposite Prepared Via the In Situ Melt Polycondensation of L-Lactic Acid in the Presence of Acidic Silica Sol : Isothermal Crystallization and Melting Behaviors , 2008 .

[10]  Hong Xu,et al.  Biodegradable Composites: Ramie Fibre Reinforced PLLA-PCL Composite Prepared by in Situ Polymerization Process , 2008 .

[11]  N. Graupner.  Application of lignin as natural adhesion promoter in cotton fibre-reinforced poly(lactic acid) (PLA) composites , 2008, Journal of Materials Science.

[12]  Jörg Müssig,et al.  Impact and tensile properties of PLA/Cordenka and PLA/flax composites , 2008 .

[13]  P. Dubois,et al.  Polylactide (PLA) designed with desired end‐use properties: 1. PLA compositions with low molecular weight ester‐like plasticizers and related performances , 2008 .

[14]  Michael P. Wolcott,et al.  Comparison of polylactide/nano-sized calcium carbonate and polylactide/montmorillonite composites: Reinforcing effects and toughening mechanisms , 2007 .

[15]  L. Turng,et al.  Solid and Microcellular Polylactide-Carbon Nanotube Nanocomposites , 2007 .

[16]  Yongjin Li,et al.  Toughening of polylactide by melt blending with a biodegradable poly(ether)urethane elastomer. , 2007, Macromolecular bioscience.

[17]  N. Nakayama,et al.  Preparation and characterization of poly(l-lactic acid)/TiO2 nanoparticle nanocomposite films with high transparency and efficient photodegradability , 2007 .

[18]  Venkatesh Balan,et al.  Effect of Ammonia Fiber Expansion (AFEX) and Silane Treatments of Corncob Granules on the Properties of Renewable Resource Based Biocomposites , 2007 .

[19]  L. Turng,et al.  Injection-Molded Solid and Microcellular Polylactide and Polylactide Nanocomposites , 2007 .

[20]  Jingbo Yin,et al.  Surface-grafted silica linked with l-lactic acid oligomer: A novel nanofiller to improve the performance of biodegradable poly(l-lactide) , 2007 .

[21]  A. Galeski,et al.  Plasticization of semicrystalline poly(l-lactide) with poly(propylene glycol) , 2006 .

[22]  M. Todo,et al.  Improvement of impact fracture properties of PLA/PCL polymer blend due to LTI addition , 2006 .

[23]  Kristiina Oksman,et al.  Mechanical Properties of Biodegradable Composites from Poly Lactic Acid (PLA) and Microcrystalline Cellulose (MCC) , 2005 .

[24]  Xuesi Chen,et al.  Grafting polymerization of L-lactide on the surface of hydroxyapatite nano-crystals , 2004 .

[25]  E. Wintermantel,et al.  Thermal and mechanical properties of plasticized poly(L‐lactic acid) , 2003 .

[26]  S. Ray,et al.  New polylactide/layered silicate nanocomposites. 5. Designing of materials with desired properties , 2003 .

[27]  P. Degée,et al.  New nanocomposite materials based on plasticized poly(l-lactide) and organo-modified montmorillonites: thermal and morphological study , 2003 .

[28]  H. Fritz,et al.  Plasticizing polylactide—the effect of different plasticizers on the mechanical properties , 1999 .

[29]  Stephen P. McCarthy,et al.  Reactive compatibilization of biodegradable blends of poly(lactic acid) and poly(ε-caprolactone) , 1998 .