Impact of P/In flux ratio and epilayer thickness on faceting for nanoscale selective area growth of InP by molecular beam epitaxy

The impact of the P/In flux ratio and the deposited thickness on the faceting of InP nanostructures selectively grown by molecular beam epitaxy (MBE) is reported. Homoepitaxial growth of InP is performed inside 200 nm wide stripe openings oriented either along a [110] or [1–10] azimuth in a 10 nm thick SiO2 film deposited on an InP(001) substrate. When varying the P/In flux ratio, no major shape differences are observed for [1–10]-oriented apertures. On the other hand, the InP nanostructure cross sections strongly evolve for [110]-oriented apertures for which (111)B facets are more prominent and (001) ones shrink for large P/In flux ratio values. These results show that the growth conditions allow tailoring the nanocrystal shape. They are discussed in the framework of the equilibrium crystal shape model using existing theoretical calculations of the surface energies of different low-index InP surfaces as a function of the phosphorus chemical potential, directly related to the P/In ratio. Experimental observations strongly suggest that the relative (111)A surface energy is probably smaller than the calculated value. We also discuss the evolution of the nanostructure shape with the InP-deposited thickness.

[1]  P. Ruterana,et al.  Influence of nanoscale faceting on the tunneling properties of near broken gap InAs/AlGaSb heterojunctions grown by selective area epitaxy , 2014, Nanotechnology.

[2]  D. Huffaker,et al.  Controlled Formation and Dynamic Wulff Simulation of Equilibrium Crystal Shapes of GaAs Pyramidal Structures on Nanopatterned Substrates , 2010 .

[3]  R. Nötzel,et al.  Impact of base size and shape on formation control of multifaceted InP nanopyramids by selective area metal organic vapor phase epitaxy , 2009 .

[4]  S. Brueck,et al.  Faceting of a quasi-two-dimensional GaAs crystal in nanoscale patterned growth , 2008 .

[5]  T. Ujihara,et al.  Pattern size effect on source supply process for sub-micrometer scale selective area growth by organometallic vapor phase epitaxy , 2006 .

[6]  S. Brueck,et al.  Epitaxial growth of a nanoscale, vertically faceted, one-dimensional, high-aspect ratio grating in III-V materials for integrated photonics , 2005 .

[7]  T. Fukui,et al.  Formation of GaAs wire structures and position-controlled In0.8Ga0.2As quantum dots on SiO2-patterned vicinal (001) GaAs substrates , 2004 .

[8]  H. Heinecke,et al.  Beam geometrical effects on planar selective area epitaxy of InPGaInAs heterostructures , 1996 .

[9]  R. Hicks,et al.  A diffusion model for selective-area epitaxy by metalorganic chemical vapor deposition , 1995 .

[10]  X. Shen,et al.  Arsenic Pressure Dependence of Surface Diffusion of Ga on Nonplanar GaAs Substrates , 1994 .

[11]  R. Matz,et al.  Evidence for Vertical Superlattices Grown by Surface Selective Growth in MOMBE (CBE) , 1992, Sixth International Conference Metalorganic Vapor Phase Epitaxy.

[12]  Klavs F. Jensen,et al.  Analysis of MOCVD of GaAs on patterned substrates , 1991 .

[13]  T. Isu,et al.  Surface diffusion length observed by in situ scanning microprobe reflection high-energy electron diffraction , 1991 .

[14]  N. Bartelt,et al.  Surface faceting and the equilibrium crystal shape , 1989 .

[15]  C. Rottman,et al.  Statistical mechanics of equilibrium crystal shapes: Interfacial phase diagrams and phase transitions , 1984 .