Long-term field and laboratory leaching tests of cemented radioactive wastes.

Experiments with real and simulated radioactive cementitious wasteforms were set up to compare the leaching behaviour of cementitious wasteforms containing nuclear power plant operational waste in field and laboratory test conditions. Experiments revealed that the average annual (137)Cs leach rate in deionised water was about thirty-five times greater compared with the measured average value for the 1st year of the field test. Cumulative leached fraction of (137)Cs for 1st year (3.74%) was close to values reported in literature for similar laboratory experiments in deionised water, however more than two orders of magnitude higher than the 1st year leached fraction of (137)Cs in the repository test (0.01%). Therefore, to compare field and laboratory test results, a scaling factor is required in order to account for surface to volume factor difference, multiplied by a temperature factor and a leach rate decrease coefficient related to the ground water composition.

[1]  E. W. Miller,et al.  Cementitious Systems for Encapsualation of Intermediate Level Waste , 2003 .

[2]  William E. Lee,et al.  An Introduction to Nuclear Waste Immobilisation , 2005 .

[3]  Fredrik P. Glasser,et al.  Application of portland cement-based materials to radioactive waste immobilization , 1992 .

[4]  A. Osmanlioglu,et al.  Immobilization of radioactive waste by cementation with purified kaolin clay. , 2002, Waste management.

[5]  Farid Benboudjema,et al.  Coupling between leaching and creep of concrete , 2008 .

[6]  M. I. Ojovan,et al.  Crystalline materials for actinide immobilisation , 2010 .

[7]  Marta Castellote,et al.  Some principles of service life calculation of reinforcements and in situ corrosion monitoring by sensors in the radioactive waste containers of El Cabril disposal (Spain) , 2006 .

[8]  F. P. Glasser,et al.  Mineralogical aspects of cement in radioactive waste disposal , 2001, Mineralogical Magazine.

[9]  F. Glasser.  Application of inorganic cements to the conditioning and immobilisation of radioactive wastes , 2011 .

[10]  Z. I. Golubeva,et al.  Evaluation of the properties of cemented radioactive wastes with prolonged testing in mound type repository , 2009 .

[11]  Qi‐Chang He,et al.  Modelling and simulations of the chemo-mechanical behaviour of leached cement-based materials: Interactions between damage and leaching , 2010 .

[12]  F. P. Glasser,et al.  Fundamental aspects of cement solidification and stabilisation , 1997 .

[13]  M. I. Ojovan,et al.  The Behaviours of Cementitious Materials in Long Term Storage and Disposal: An Overview of Results of the IAEA Coordinated Research Project , 2009 .

[14]  M. I. Ojovan,et al.  Handbook of advanced radioactive waste conditioning technologies , 2011 .

[15]  Jack M. Chi,et al.  Effects of Carbonation on Mechanical Properties and Durability of Concrete Using Accelerated Testing Method , 2002 .

[16]  M. Moranville,et al.  Material and Environmental Parameter Effects on the Leaching of Cement Pastes: Experiments and Modelling , 2008 .

[17]  M. I. Ojovan,et al.  Alkali ion exchange in γ-irradiated glasses , 2004 .

[18]  Rehab O. Abdel Rahman,et al.  Modeling the long-term leaching behavior of (137)Cs, (60)Co, and (152,154)Eu radionuclides from cement-clay matrices. , 2007, Journal of hazardous materials.

[19]  Rehab O. Abdel Rahman,et al.  Assessment of the leaching characteristics of incineration ashes in cement matrix , 2009 .

[20]  M. I. Ojovan,et al.  Waste glass behavior in a loamy soil of a wet repository site , 2001 .

[21]  R. S. Pavlovic,et al.  Mortar-Radwaste Mixture Form Characterization Due to 137 Cs Leach-Rate Using Accelerated Ageing Processes , 1993 .

[22]  F. Glasser.  Characterisation of the Barrier Performance of Cements , 2002 .

[23]  M. I. Ojovan,et al.  Corrosion of low level vitrified radioactive waste in a loamy soil , 2006 .

[24]  M. I. Ojovan,et al.  39-years performance of cemented radioactive waste in a mound type repository , 2006 .

[25]  C. Cau Dit Coumes,et al.  Cementation of a low-level radioactive waste of complex chemistry , 2003 .

[26]  I. Plećaš,et al.  Leaching behavior of 60Co and 137Cs from spent ion exchange resins in cement–bentonite clay matrix , 2004 .

[27]  J. Sercombe,et al.  Modelling of radionuclide release from a concrete container , 2007 .

[28]  Gary F. Bennett,et al.  International basic safety standards for protection against ionizing radiation of and for the safety of radiation sources , 1996 .

[29]  E. P. Goldfinch,et al.  Containers for Packaging of Solid Low and Intermediate Level Radioactive Wastes — IAEA Technical Reports Series NO. 355. , 1993 .

[30]  David K. Peeler,et al.  Performance of a buried radioactive high level waste (HLW) glass after 24 years , 2008 .