Study of HPHT single crystal diamond as precision cutting tool material

Abstract High pressure high temperature (HPHT) synthetic diamond is rapidly replacing natural diamond in precision machining industry due to its consistency in quality and cost. It is believed by some manufacturers that HPHT diamond cutting tool is virtually free of impurities, inclusions and cracks. This paper is to analyze defects inside HPHT diamond crystal by density test, optical microscopy, SEM, Raman, and XRD. Results show that HPHT diamond is relatively clean, with less chemical elements inside in comparison with natural diamond. However, there are cracks, pit holes, and bubbles in/on the crystal, some tracing amount of cementite (Fe 3 C), γ-Fe, and nickel based carbides also exist in the HPHT diamond crystal, causing less accurate cutting tool edge and surface integrity. Residual stresses in HPHT diamond are compressive but high in value, may lead to cutting tool brittleness and micro-chipping, which is a common reason for diamond tool failing in precision machining.

[1]  J. Cohen,et al.  Residual Stress: Measurement by Diffraction and Interpretation , 1987 .

[2]  S. Serrano,et al.  SEM and Raman analysis of boron-doped diamond coating on spherical textured substrates , 2006 .

[3]  J. Field.  The Properties of natural and synthetic diamond , 1992 .

[4]  S. Prawer,et al.  Raman spectroscopy of diamond and doped diamond , 2004, Philosophical Transactions of the Royal Society of London. Series A: Mathematical, Physical and Engineering Sciences.

[5]  P. May,et al.  Graphite-to-diamond transformation induced by ultrasound cavitation , 2008 .

[6]  R. Abbaschian,et al.  Recent Progress in Growth of Diamond Crystals , 2005 .

[7]  Amanda Yarnell,et al.  THE MANY FACETS OF MAN-MADE DIAMONDS , 2004 .

[8]  M. Prelas,et al.  Handbook of Industrial Diamonds and Diamond Films , 2018 .

[9]  Christopher J. Evans,et al.  Application of precision diamond machining to the manufacture of microphotonics components , 2003, SPIE Optics + Photonics.

[10]  V. Turkevich,et al.  Innovative Superhard Materials and Sustainable Coatings for Advanced Manufacturing , 2005 .

[11]  J. Ager,et al.  Effect of intrinsic growth stress on the Raman spectra of vacuum‐arc‐deposited amorphous carbon films , 1995 .

[12]  T. R. Anthony,et al.  Stresses generated by inhomogeneous distributions of inclusions in diamonds , 1997 .

[13]  P. Houtte,et al.  Comparative measurement of residual stress in diamond coatings by low-incident-beam-angle-diffraction and micro-Raman spectroscopy , 1996 .

[14]  J. Celis,et al.  Residual stresses of diamond and diamondlike carbon films , 2005 .

[15]  F. Bundy,et al.  Man-Made Diamonds , 1955, Nature.

[16]  The Influence of Cutting Edge Quality on Workpiece Roughness in Diamond Turning Process , 1993 .