The effect of moisture content on the corrosion of fasteners embedded in wood subjected to alkaline copper quaternary treatment

Abstract This paper characterizes the corrosion rate of embedded fasteners as a function of wood moisture content using gravimetric and electrochemical measurements. The results indicated that the corrosion rate increased with moisture content before reaching a plateau. The phases present in the corrosion products, as analyzed using X-ray diffraction, are generally consistent with previous work. Uniform corrosion was observed for all fasteners and all conditions except steel fasteners embedded in water-saturated wood. Data of dependence of corrosion rate on moisture content, presented herein, are necessary to ensure the accuracy of combined hygrothermal/corrosion models used to predict durability of wood structures.

[1]  X. G. Zhang,et al.  Corrosion of Zinc and Zinc Alloys , 2005 .

[2]  Samuel V. Glass,et al.  Moisture relations and physical properties of wood , 2010 .

[3]  F. Walsh,et al.  Direct-Current Methods for the Estimation of Corrosion Rates in Aqueous Timber Preservatives , 2008 .

[4]  R. Farmer.  Corrosion of Metals in Association with Wood , 1967 .

[5]  D. R. Rammer,et al.  Optical method for measuring the surface area of a threaded fastener , 2009 .

[6]  J. K. Dennis,et al.  Corrosion Resistance of Zinc-alloy Coated Steel in Construction Industry Environments , 1997 .

[7]  A. Baker,et al.  Corrosion of nails in CCA- and ACA-treated wood in two environments , 1992 .

[8]  A. Baker,et al.  Corrosion of metal in wood products , 1980 .

[9]  Florian Mansfeld,et al.  Tafel Slopes and Corrosion Rates from Polarization Resistance Measurements , 1973 .

[10]  G. Kear,et al.  Corrosion of ferrous- and zinc-based materials in CCA, ACQ and CuAz timber preservative aqueous solutions , 2008 .

[11]  Margaret P. Hamel,et al.  Wood protection techniques and the use of treated wood in construction , 1988 .

[12]  Douglas R. Rammer,et al.  Electrochemical corrosion testing of fasteners in extracts of treated wood , 2008 .

[13]  F. Mansfeld.  Simultaneous Determination of Instantaneous Corrosion Rates and Tafel Slopes from Polarization Resistance Measurements , 1973 .

[14]  S. Esterby.  American Society for Testing and Materials , 2006 .

[15]  R. Baechler.  Corrosion of Metal Fastenings in Zinc-Chloride-Treated Wood , 1934 .

[16]  G. Kear,et al.  Weight loss studies of fastener materials corrosion in contact with timbers treated with copper azole and alkaline copper quaternary compounds , 2009 .

[17]  Zinc Alloy Coated Steel Sheet,et al.  Proceedings : 4th International Conference on Zinc and Zinc Alloy Coated Steel Sheet : GALVATECH '98 : September 20-23, 1998, Makuhari, Chiba, Japan , 1998 .

[18]  S. Zelinka.  Corrosion of Embedded Metals in Wood: An Overview of Recent Research with Implications for building moisture design , 2013 .

[19]  Douglas R. Rammer,et al.  Corrosion Rates of Fasteners in Treated Wood Exposed to 100% Relative Humidity , 2009 .

[20]  Douglas R. Rammer,et al.  Direct current testing to measure corrosiveness of wood preservatives , 2007 .

[21]  Analytical Determination of the Surface Area of a Threaded Fastener , 2008 .

[22]  A. Baker,et al.  Corrosion of metals in preservative-treated wood , 2012 .

[23]  Dominique Derome,et al.  Combining hygrothermal and corrosion models to predict corrosion of metal fasteners embedded in wood , 2011 .

[24]  F. Walsh,et al.  Impedance spectroscopy studies of the dissolution of ferrous- and zinc-based materials in aqueous timber preservatives , 2008 .

[25]  Robert H. Falk,et al.  Fasteners for Exposed Wood Structures , 1991 .

[26]  J. K. Dennis,et al.  Corrosion behaviour of zinc and zinc alloy coated steel in preservative treated timber , 1995 .

[27]  D. Stone,et al.  Corrosion of metals in wood: Comparing the results of a rapid test method with long-term exposure tests across six wood treatments , 2011 .

[28]  Donald S. Stone,et al.  Exposure testing of fasteners in preservative treated wood: Gravimetric corrosion rates and corrosion product analyses , 2010 .

[29]  D. Rammer,et al.  EQUIVALENT CIRCUIT MODELING OF WOOD AT 12% MOISTURE CONTENT , 2007 .

[30]  D. Rammer,et al.  Synthesis of published and unpublished corrosion data from long term tests of fasteners embedded in wood : calculation of corrosion rates and the effect of corrosion on lateral joint strength , 2011 .