Room temperature operation of quantum cascade lasers monolithically integrated onto a lattice-mismatched substrate

We report the experimental results of a 40-stage InP-based quantum cascade laser (QCL) structure grown on a 6-inch GaAs substrate with metamorphic buffer (M-buffer). The laser structure’s strain-balanced active region was composed of Al0.78In0.22As/In0.73Ga0.27As and an all-InP, 8 μm-thick waveguide. The wafer was processed into ridge-waveguide chips (3mm x 30 μm devices) with lateral current injection scheme. Devices with high reflection coating delivered power in excess of 200 mW of total peak power at 78K, with lasing observed up to 230K. Preliminary reliability testing at maximum power showed no sign of performance degradation after 200 minutes of runtime. Measured characteristic temperatures of T0 ≈ 460 K and T1 ≈ 210 K describes the temperature dependence for threshold current and slope efficiency, respectively, in the range from 78K to 230K. Partial high reflection coating was used on the front facet to extend the lasing range up to 303K.

[1]  G. G. Stokes.  "J." , 1890, The New Yale Book of Quotations.

[2]  N. D. Durie,et al.  Digest of papers , 1976 .

[3]  Chikara Amano,et al.  Efficiency calculations of thin‐film GaAs solar cells on Si substrates , 1985 .

[4]  Y. Cordier,et al.  InAlAs buffer layers grown lattice mismatched on GaAs with inverse steps , 1999 .

[5]  W. K. Liu,et al.  Strain relaxation and dislocation filtering in metamorphic high electron mobility transistor structures grown on GaAs substrates , 2001 .

[6]  Andrew G. Glen,et al.  APPL , 2001 .

[7]  Mattias Beck,et al.  Quantum-cascade-laser structures as photodetectors , 2002 .

[8]  J. Chauveau,et al.  Interplay between relaxation, surface morphology and composition modulation in InAlAs graded buffer layers , 2003 .

[9]  Dmitri Lubyshev,et al.  Comparison of As- and P-based metamorphic buffers for high performance InP heterojunction bipolar transistor and high electron mobility transistor applications , 2004 .

[10]  Werner Schrenk,et al.  Low divergence single-mode surface emitting quantum cascade ring lasers , 2008 .

[11]  J. Faist,et al.  Mid-infrared frequency comb based on a quantum cascade laser , 2012, Nature.

[12]  J. Bowers,et al.  Hybrid Silicon Photonic Integrated Circuit Technology , 2013, IEEE Journal of Selected Topics in Quantum Electronics.

[13]  L. Mawst,et al.  InGaAs/AlInAs strain-compensated Superlattices grown on metamorphic buffer layers for low-strain, 3.6 μm-emitting quantum-cascade-laser active regions , 2013 .

[14]  J. Koenderink.  Q… , 2014, Les noms officiels des communes de Wallonie, de Bruxelles-Capitale et de la communaute germanophone.

[15]  John E. Bowers,et al.  High performance continuous wave 1.3 μm quantum dot lasers on silicon , 2014 .

[16]  L. Mawst,et al.  Regrowth of quantum cascade laser active regions on metamorphic buffer layers , 2016 .

[17]  Arkadiy Lyakh,et al.  5.6 μm quantum cascade lasers based on a two-material active region composition with a room temperature wall-plug efficiency exceeding 28% , 2016 .

[18]  William W. Bewley,et al.  Quantum cascade laser on silicon , 2016 .