Nucleation of precipitates in aged Al-Cu-Mg-(Ag) alloys with high Cu:Mg ratios

Abstract Clustering and precipitation reactions during the early stages of ageing at 180°C in an Al 1.7Cu 0.3Mg (at.%) alloy and equivalent alloys containing 0.1 and 0.2 at.% Ag have been studied. Transmission electron microscopy, electron diffraction and atom probe field ion microscopy have been used to clarify the precipitation processes in these alloys following ageing for 15, 30, 120, 720 and 9000 s. Reactions involving the formation of Mg and Mg Cu co-clusters were observed in the ternary Al Cu Mg alloy whereas Mg, Ag and Mg Ag co-clusters were found to co-exist with Cu-clusters in the quaternary Al Cu Mg Ag alloy. Results indicate that the Mg Ag interaction is strong and it is proposed that the role of Ag in quaternary alloys is to effectively trap Mg atoms, resulting in Mg Ag co-clusters, which provide favorable sites for nucleation of the Ω phase. Various models for precursor phases have also been examined. Apart from the presence of Mg Ag co-clusters, no evidence of a distinct precursor phase was observed.