Spark Plasma Sintering (SPS) has been successfully applied in the sintering of nanocrystalline BaTiO3 and γ-Al2O3 in order to reach fully dense nanostructured ceramics at moderate pressure and temperature. BaTiO3 compacts with densities exceeding 97% and grain size of 50 nm have thus been prepared at temperatures not exceeding 850 oC using a uniaxial pressure of 100MPa. The selection of sintering temperature is critical for the purpose of minimizinggrain growth and there is a demarcation temperature (820 oC) between normal and abnormal grain growth for the nanocrystalline BaTiO3 powder used in this study. Fully dense α-Al2O3 compacts containing grains of the size 300nm or less were consolidated from high-purity γ-Al2O3 powders without the use of additives or seeds. The transition temperature of γ-Al2O3 to α-Al2O3 can be lowered to 960 oC when γ-Al2O3 powder is compacted in the SPS apparatus. The possible mechanisms related to this low transition temperature and to the sintering of both BaTiO3 and γ-Al2O3 are discussed with special reference to the effect of the pulsed electric field generated by the pulsed electrical current used to heat the sample
[1]
P. Bowen,et al.
From powders to sintered pieces: forming, transformations and sintering of nanostructured ceramic oxides
,
2002
.
[2]
P. Bowen,et al.
Synthesis of Barium Titanate Powders by Low-Temperature Aqueous Synthesis Using a New Segmented Flow Tubular Reactor
,
2001
.
[3]
L. Gauckler,et al.
Sintering of Nanocrystalline CeO2 Ceramics
,
2001
.
[4]
D. Sinclair,et al.
Spark-plasma-sintering of fine BaTiO3 powder prepared by a sol-crystal method
,
2001
.
[5]
I. Chen,et al.
Sintering dense nanocrystalline ceramics without final-stage grain growth
,
2000,
Nature.
[6]
B. Kear,et al.
High pressure/low temperature sintering of nanocrystalline alumina
,
1998
.
[7]
Moon J. Kim,et al.
Retention of nanostructure in aluminum oxide by very rapid sintering at 1150 °C
,
1995
.
[8]
Suzana Caetano da Silva Lannes,et al.
Powder Technology
,
2020,
Nature.