Electrochemical properties of ZrO2-doped V2O5 amorphous powders with spherical shape and fine size.

Amorphous V2O5 powders with zirconia (ZrO2) dopant are prepared by one-pot spray pyrolysis at temperatures above the melting temperature of V2O5. The powders with 7 wt % ZrO2 are completely spherical and dense with a clean surface, on which crystals of pure V2O5 powders are scarcely observed. The V2O5 powders with 7 wt % ZrO2 have uniformly distributed V and Zr components. The uniformly distributed Zr component disturbs the crystallization of V2O5 during the quenching of the melted powders. These powders also give smooth initial discharge curves with a single slope, which is typical to amorphous materials. The discharge capacities of the V2O5 powders with 7 wt % ZrO2 are 309, 269, and 222 mA h g(-1) after the first, second, and 50th cycles, respectively, even at a high current density of 294 mA g(-1). The capacity retention measured after the first cycle is 83% after 50 cycles.

[1]  Y. Kang,et al.  Electrochemical properties of spherically shaped dense V2O5 cathode powders prepared directly by spray pyrolysis , 2012 .

[2]  X. Lou,et al.  Synthesis of hierarchical three-dimensional vanadium oxide microstructures as high-capacity cathode materials for lithium-ion batteries. , 2012, ACS applied materials & interfaces.

[3]  G. Cao,et al.  Mesoporous vanadium pentoxide nanofibers with significantly enhanced Li-ion storage properties by electrospinning , 2011 .

[4]  Jun Liu,et al.  Facile synthesized nanorod structured vanadium pentoxide for high-rate lithium batteries , 2010 .

[5]  Haoshen Zhou,et al.  Centimeter‐Long V2O5 Nanowires: From Synthesis to Field‐Emission, Electrochemical, Electrical Transport, and Photoconductive Properties , 2010, Advanced materials.

[6]  Anne C. Dillon,et al.  Layered vanadium and molybdenum oxides: batteries and electrochromics , 2009 .

[7]  D. Wexler,et al.  High Capacity, Safety, and Enhanced Cyclability of Lithium Metal Battery Using a V2O5 Nanomaterial Cathode and Room Temperature Ionic Liquid Electrolyte , 2008 .

[8]  Zaiping Guo,et al.  Synthesis of spherical porous vanadium pentoxide and its electrochemical properties , 2008 .

[9]  Heng Liu,et al.  Preparation and electrochemical properties of submicron spherical V2O5 as cathode material for lithium ion batteries , 2008 .

[10]  D. Wexler,et al.  Synthesis and electrochemical properties of V2O5 nanostructures prepared via a precipitation process for lithium-ion battery cathodes , 2007 .

[11]  Linda F. Nazar,et al.  Review on electrode–electrolyte solution interactions, related to cathode materials for Li-ion batteries , 2007 .

[12]  R. Torresi,et al.  Electrochemical and morphological stabilization of V2O5 nanofibers by the addition of polyaniline , 2007 .

[13]  Yi Cui,et al.  Fast, completely reversible li insertion in vanadium pentoxide nanoribbons. , 2007, Nano letters.

[14]  B. Dunn,et al.  Preparation of Nanotextured VO2[B] from Vanadium Oxide Aerogels , 2006 .

[15]  Ying Wang,et al.  Nanostructured Vanadium Oxide Electrodes for Enhanced Lithium‐Ion Intercalation , 2006 .

[16]  Li-Jun Wan,et al.  Self-assembled vanadium pentoxide (V2O5) hollow microspheres from nanorods and their application in lithium-ion batteries. , 2005, Angewandte Chemie.

[17]  G. Cao,et al.  Synthesis and electrochemical properties of vanadium pentoxide nanotube arrays. , 2005, The journal of physical chemistry. B.

[18]  D. Aurbach,et al.  Surface films phenomena on vanadium-pentoxide cathodes for Li and Li-ion batteries: in situ AFM imaging , 2004 .

[19]  B. Dunn,et al.  Synthesis and Electrochemical Properties of Vanadium Oxide Aerogels Prepared by a Freeze-Drying Process , 2004 .

[20]  Min Gyu Kim,et al.  Li + Storage Sites in Amorphous V 2 O 5 Prepared by Precipitation Method , 2003 .

[21]  C. E. Tracy,et al.  Improving the durability of amorphous vanadium oxide thin-film electrode in a liquid electrolyte , 2003 .

[22]  T. Seong,et al.  Effect of platinum co-sputtering on characteristics of amorphous vanadium oxide films , 2002 .

[23]  S. Passerini,et al.  Lithium ion insertion in porous metal oxides , 1999 .

[24]  D. W. Readey,et al.  Li ion diffusion measurements in V2O5 and Li(Co1−xAlx)O2 thin-film battery cathodes , 1999 .

[25]  S. Passerini,et al.  A 400 mAh/g aerogel-like V2O5 cathode for rechargeable lithium batteries , 1998 .

[26]  M. Ward,et al.  V 2 O 5 Xerogel Films as Intercalation Hosts for Lithium I . Insertion Stoichiometry, Site Concentration, and Specific Energy , 1995 .

[27]  S. Passerini,et al.  Stress and electrochromism induced by Li insertion in crystalline and amorphous V2O5 thin film electrodes , 1993 .

[28]  Weiyang Li,et al.  Electrochemical Lithium Intercalation/Deintercalation of Single-Crystalline V2O5 Nanowires , 2007 .