Utilization of fly ash with silica fume and properties of Portland cement–fly ash–silica fume concrete

Abstract This paper reports the normal consistency, setting time, workability and compressive strength results of Portland cement–fly ash–silica fume systems. The results show that water requirement for normal consistency was found to increase with increasing SF content while a decrease in initial setting time was found. Workability, measured in term of slump, was found to decrease with silica fume content (compared to blends without silica fume). However, it must be noted that despite the reduction in the slump values, the workability of Portland cement–fly ash–silica fume concrete in most cases remained higher than that of the Portland cement control concrete. Furthermore, the utilization of silica fume with fly ash was found to increase the compressive strength of concrete at early ages (pre 28 days) up to 145% with the highest strength obtained when silica fume was used at 10 wt%. Moreover, scanning electron micrographs show that utilization of fly ash with silica fume resulted in a much denser microstructure, thereby leading to an increase in compressive strength.

[1]  A. Neville.  Properties of Concrete , 1968 .

[2]  K. Wesche.  Fresh mortar and concrete with fly ash , 1991 .

[3]  W J Halstead,et al.  USE OF FLY ASH IN CONCRETE , 1986 .

[4]  V. M. Malhotra,et al.  Condensed Silica Fume in Concrete , 1987 .

[5]  Ramazan Demirboga,et al.  Thermal conductivity and compressive strength of concrete incorporation with mineral admixtures , 2007 .

[6]  R. Helmuth,et al.  Fly Ash in Cement and Concrete , 1987 .

[7]  P. Basheer,et al.  Potential use of spent mushroom compost ash as an activator for pulverised fuel ash , 2005 .

[8]  Halit Yazıcı,et al.  The effect of curing conditions on compressive strength of ultra high strength concrete with high volume mineral admixtures , 2007 .

[9]  Tahir Kemal Erdem,et al.  Use of binary and ternary blends in high strength concrete , 2008 .

[10]  Halit Yazici,et al.  Utilization of fly ash and ground granulated blast furnace slag as an alternative silica source in reactive powder concrete , 2008 .

[11]  C. Shi.  Early microstructure development of activated lime-fly ash pastes , 1996 .

[12]  V. Papadakis.  Effect of fly ash on Portland cement systems. Part II. High-calcium fly ash , 1999 .

[13]  V. Malhotra,et al.  Fly ash in concrete , 1986 .

[14]  C. Poon,et al.  Activation of fly ash/cement systems using calcium sulfate anhydrite (CaSO4) , 2001 .

[15]  J. Ayala,et al.  The effect of mechanically and chemically activated fly ashes on mortar properties , 2006 .

[16]  Caijun Shi,et al.  Acceleration of the reactivity of fly ash by chemical activation , 1995 .

[17]  J. Brooks,et al.  Effect of admixtures on the setting times of high-strength concrete , 2000 .