Fabrication and characterization of poly(propylene fumarate) scaffolds with controlled pore structures using 3-dimensional printing and injection molding.

Poly(propylene fumarate) (PPF) is an injectable, biodegradable polymer that has been used for fabricating preformed scaffolds in tissue engineering applications because of in situ crosslinking characteristics. Aiming for understanding the effects of pore structure parameters on bone tissue ingrowth, 3-dimensional (3D) PPF scaffolds with controlled pore architecture have been produced in this study from computer-aided design (CAD) models. We have created original scaffold models with 3 pore sizes (300, 600, and 900 microm) and randomly closed 0%, 10%, 20%, or 30% of total pores from the original models in 3 planes. PPF scaffolds were fabricated by a series steps involving 3D printing of support/build constructs, dissolving build materials, injecting PPF, and dissolving support materials. To investigate the effects of controlled pore size and interconnectivity on scaffolds, we compared the porosities between the models and PPF scaffolds fabricated thereby, examined pore morphologies in surface and cross-section using scanning electron microscopy, and measured permeability using the falling head conductivity test. The thermal properties of the resulting scaffolds as well as uncrosslinked PPF were determined by differential scanning calorimetry and thermogravimetric analysis. Average pore sizes and pore shapes of PPF scaffolds with 600- and 900-microm pores were similar to those of CAD models, but they depended on directions in those with 300-microm pores. Porosity and permeability of PPF scaffolds decreased as the number of closed pores in original models increased, particularly when the pore size was 300 microm as the result of low porosity and pore occlusion. These results show that 3D printing and injection molding technique can be applied to crosslinkable polymers to fabricate 3D porous scaffolds with controlled pore structures, porosity, and permeability using their CAD models.

[1]  W. Hayes,et al.  Characterization of partially saturated poly(propylene fumarate) for orthopaedic application. , 1997, Journal of biomaterials science. Polymer edition.

[2]  L. Bonassar,et al.  Direct perfusion measurements of cancellous bone anisotropic permeability. , 2001, Journal of biomechanics.

[3]  A. Mikos,et al.  Marrow stromal osteoblast function on a poly(propylene fumarate)/beta-tricalcium phosphate biodegradable orthopaedic composite. , 2000, Biomaterials.

[4]  C. M. Agrawal,et al.  Biodegradable polymeric scaffolds for musculoskeletal tissue engineering. , 2001, Journal of biomedical materials research.

[5]  S. E. Feinberg,et al.  Hydroxyapatite implants with designed internal architecture , 2001, Journal of materials science. Materials in medicine.

[6]  B L Currier,et al.  Biodegradable Polymer Scaffolds for Cartilage Tissue Engineering , 2001, Clinical orthopaedics and related research.

[7]  Joo L. Ong,et al.  Diffusion in Musculoskeletal Tissue Engineering Scaffolds: Design Issues Related to Porosity, Permeability, Architecture, and Nutrient Mixing , 2004, Annals of Biomedical Engineering.

[8]  A. Mikos,et al.  Crosslinking characteristics of an injectable poly(propylene fumarate)/β‐tricalcium phosphate paste and mechanical properties of the crosslinked composite for use as a biodegradable bone cement , 1999 .

[9]  Lichun Lu,et al.  A Biodegradable and Cross-Linkable Multiblock Copolymer Consisting of Poly(propylene fumarate) and Poly(ε-caprolactone): Synthesis, Characterization, and Physical Properties , 2005 .

[10]  A. Domb,et al.  Biodegradable bone cement compositions based on acrylate and epoxide terminated poly(propylene fumarate) oligomers and calcium salt compositions. , 1996, Biomaterials.

[11]  E. Sachlos,et al.  ON THE APPLICATION OF SOLID FREEFORM FABRICATION TECHNOLOGY TO THE PRODUCTION OF TISSUE ENGINEERING SCAFFOLDS , 2022 .

[12]  W. Hayes,et al.  The ingrowth of new bone tissue and initial mechanical properties of a degrading polymeric composite scaffold. , 1995, Tissue engineering.

[13]  D. Kaplan,et al.  Porosity of 3D biomaterial scaffolds and osteogenesis. , 2005, Biomaterials.

[14]  David P. Martin,et al.  Application of Stereolithography for Scaffold Fabrication for Tissue Engineered Heart Valves , 2002, ASAIO journal.

[15]  A. Mikos,et al.  Synthesis of biodegradable poly(propylene fumarate) networks with poly(propylene fumarate)–diacrylate macromers as crosslinking agents and characterization of their degradation products , 2001 .

[16]  S. Hollister,et al.  Optimal design and fabrication of scaffolds to mimic tissue properties and satisfy biological constraints. , 2002, Biomaterials.

[17]  A J Verbout,et al.  Design and fabrication of standardized hydroxyapatite scaffolds with a defined macro-architecture by rapid prototyping for bone-tissue-engineering research. , 2004, Journal of biomedical materials research. Part A.

[18]  Andreas Hein,et al.  Application of stereolithography for scaffold fabrication for tissue engineered heart valves. , 2000 .

[19]  J. Fisher,et al.  Soft and hard tissue response to photocrosslinked poly(propylene fumarate) scaffolds in a rabbit model. , 2002, Journal of biomedical materials research.

[20]  Dietmar W Hutmacher,et al.  Scaffold-based tissue engineering: rationale for computer-aided design and solid free-form fabrication systems. , 2004, Trends in biotechnology.

[21]  P H Krebsbach,et al.  Indirect solid free form fabrication of local and global porous, biomimetic and composite 3D polymer-ceramic scaffolds. , 2003, Biomaterials.

[22]  Malcolm N. Cooke,et al.  Use of stereolithography to manufacture critical-sized 3D biodegradable scaffolds for bone ingrowth. , 2003, Journal of biomedical materials research. Part B, Applied biomaterials.

[23]  H. Takita,et al.  Pore size of porous hydroxyapatite as the cell-substratum controls BMP-induced osteogenesis. , 1997, Journal of biochemistry.

[24]  B Derby,et al.  Novel collagen scaffolds with predefined internal morphology made by solid freeform fabrication. , 2003, Biomaterials.

[25]  K. Leong,et al.  The design of scaffolds for use in tissue engineering. Part II. Rapid prototyping techniques. , 2002, Tissue engineering.

[26]  S F Hulbert,et al.  Potential of ceramic materials as permanently implantable skeletal prostheses. , 1970, Journal of biomedical materials research.

[27]  C. M. Agrawal,et al.  New technique to extend the useful life of a biodegradable cartilage implant. , 1998, Tissue engineering.

[28]  G. Daculsi,et al.  Macroporous biphasic calcium phosphate ceramics: influence of macropore diameter and macroporosity percentage on bone ingrowth. , 1998, Biomaterials.

[29]  M J Yaszemski,et al.  Polymer concepts in tissue engineering. , 1998, Journal of biomedical materials research.

[30]  G. Kharas,et al.  Synthesis and characterization of fumarate-based polyesters for use in bioresorbable bone cement composites , 1997 .

[31]  Amit Bandyopadhyay,et al.  Processing and characterization of porous alumina scaffolds , 2002, Journal of materials science. Materials in medicine.

[32]  M J Grimm,et al.  Measurements of permeability in human calcaneal trabecular bone. , 1997, Journal of biomechanics.

[33]  Scott J Hollister,et al.  Mechanical and in vivo performance of hydroxyapatite implants with controlled architectures. , 2002, Biomaterials.

[34]  Wei Sun,et al.  Recent development on computer aided tissue engineering - a review , 2002, Comput. Methods Programs Biomed..

[35]  A. Mikos,et al.  Injectable biodegradable materials for orthopedic tissue engineering. , 2000, Biomaterials.

[36]  S. Suzuki,et al.  Bilateral Humeral Lengthening in Achondroplasia , 2001, Clinical orthopaedics and related research.

[37]  K. Leong,et al.  Solid freeform fabrication of three-dimensional scaffolds for engineering replacement tissues and organs. , 2003, Biomaterials.

[38]  David Dean,et al.  Synthesis and properties of photocross-linked poly(propylene fumarate) scaffolds , 2001, Journal of biomaterials science. Polymer edition.

[39]  P. Layrolle,et al.  Macroporous biphasic calcium phosphate scaffold with high permeability/porosity ratio. , 2003, Tissue engineering.