Molecular Mobility of Amorphous Pharmaceutical Solids Below Their Glass Transition Temperatures

AbstractPurpose. To measure the molecular mobility of amorphous pharmaceutical solids below their glass transition temperatures (Tg), using indomethacin, poly (vinyl pyrrolidone) (PVP) and sucrose as model compounds. Methods. Differential scanning calorimetry (DSC) was used to measure enthalpic relaxation of the amorphous samples after storage at temperatures 16-47 K below Tg for various time periods. The measured enthalpy changes were used to calculate molecular relaxation time parameters. Analogous changes in specimen dimensions were measured for PVP films using thermomechanical analysis. Results. For all the model materials it was necessary to cool to at least 50 K below the experimental Tg before the molecular motions detected by DSC could be considered to be negligible over the lifetime of a typical pharmaceutical product. In each case the temperature dependence of the molecular motions below Tg was less than that typically reported above Tg and was rapidly changing. Conclusions. In the temperature range studied the model amorphous solids were in a transition zone between regions of very high molecular mobility above Tg and very low molecular mobility much further below Tg. In general glassy pharmaceutical solids should be expected to experience significant molecular mobility at temperatures up to fifty degrees below their glass transition temperature.

[1]  A. Saleki-Gerhardt,et al.  Assessment of disorder in crystalline solids , 1994 .

[2]  Y. Nakamura,et al.  Glassy state of pharmaceuticals. IV. Studies on glassy pharmaceuticals by thermomechanical analysis. , 1989, Chemical & pharmaceutical bulletin.

[3]  G. Zografi,et al.  Molecular Mobility in Mixtures of Absorbed Water and Solid Poly(vinylpyrrolidone) , 1993, Pharmaceutical Research.

[4]  J. H. Gibbs,et al.  Nature of the Glass Transition and the Glassy State , 1958 .

[5]  L. Slade,et al.  Glass transitions and water-food structure interactions. , 1995, Advances in food and nutrition research.

[6]  Bruno C. Hancock,et al.  Crystallization of indomethacin from the amorphous state below and above its glass transition temperature. , 1994, Journal of pharmaceutical sciences.

[7]  S. Montserrat Physical aging studies in epoxy resins. I. Kinetics of the enthalpy relaxation process in a fully cured epoxy resin , 1994 .

[8]  C. Angell,et al.  Strong and Fragile Behavior in Liquid Polymers , 1990 .

[9]  L. Struik Physical aging in amorphous polymers and other materials , 1978 .

[10]  C. Angell,et al.  Nonexponential relaxations in strong and fragile glass formers , 1993 .

[11]  W. Kauzmann The Nature of the Glassy State and the Behavior of Liquids at Low Temperatures. , 1948 .

[12]  C. Angell,et al.  Liquid fragility and the glass transition in water and aqueous solutions , 1994 .

[13]  A. Piccolo,et al.  The dynamic glass transition of a 'fragile' molecular liquid in the megahertz domain , 1994 .

[14]  A. Barlow,et al.  Viscous behaviour of supercooled liquids , 1966, Proceedings of the Royal Society of London. Series A. Mathematical and Physical Sciences.

[15]  K. Ngai,et al.  Normalization of the temperature dependence of segmental relaxation times , 1992 .

[16]  R. Landel,et al.  The Temperature Dependence of Relaxation Mechanisms in Amorphous Polymers and Other Glass-Forming Liquids , 1955 .

[17]  Graham Williams,et al.  Non-symmetrical dielectric relaxation behaviour arising from a simple empirical decay function , 1970 .

[18]  J. C. Tucker,et al.  Dependence of the glass transition temperature on heating and cooling rate , 1974 .

[19]  J. H. Guo A theoretical and experimental study of additive effects of physical aging and antiplasticization on the water permeability of polymer film coatings. , 1994, Journal of pharmaceutical sciences.

[20]  J. Cowie,et al.  Physical ageing of poly(methyl methacrylate) from enthalpy relaxation measurements , 1993 .