Direct Imaging of Cl‐ and Cu‐Induced Short‐Circuit Efficiency Changes in CdTe Solar Cells

To achieve high-efficiency polycrystalline CdTe-based thin-film solar cells, the CdTe absorbers must go through a post-deposition CdCl2 heat treatment followed by a Cu diffusion step. To better understand the roles of each treatment with regard to improving grains, grain boundaries, and interfaces, CdTe solar cells with and without Cu diffusion and CdCl2 heat treatments are investigated using cross-sectional electron beam induced current, electron backscatter diffraction, and scanning transmission electron microscope techniques. The evolution of the cross-sectional carrier collection profile due to these treatments that cause an increase in short-circuit current and higher open-circuit voltage are identified. Additionally, an increased carrier collection in grain boundaries after either/both of these treatments is revealed. The increased current at the grain boundaries is shown to be due to the presence of a space charge region with an intrinsic carrier collection profile width of ≈350 nm. Scanning transmission electron microscope electron-energy loss spectroscopy shows a decreased Te and increased Cl concentration in grain boundaries after treatment, which causes the inversion. Furthermore, each treatment improves the overall carrier collection efficiency of the cell separately, and, therefore, the benefits realized by each treatment are shown to be independent of each other.

[1]  David Cahen,et al.  Understanding the Beneficial Role of Grain Boundaries in Polycrystalline Solar Cells from Single‐Grain‐Boundary Scanning Probe Microscopy , 2006 .

[2]  N. Y. Canli,et al.  Diffusion and influence of Cu on properties of CdTe thin films and CdTe/CdS cells , 2005 .

[3]  J. Sites,et al.  Copper inclusion and migration from the back contact in CdTe solar cells , 2004 .

[4]  Yanfa Yan,et al.  Fabrication and characterization of high-efficiency CdTe-based thin-film solar cells on commercial SnO2:F-coated soda-lime glass substrates , 2013 .

[5]  B. Hamadani,et al.  Local electrical characterization of cadmium telluride solar cells using low-energy electron beam , 2013 .

[6]  N. Jokerst,et al.  Copper migration in cdte heterojunction solar cells , 1996 .

[7]  Sidney R. Cohen,et al.  Direct evidence for grain-boundary depletion in polycrystalline CdTe from nanoscale-resolved measurements , 2003 .

[8]  Suhuai Wei,et al.  Research strategies toward improving thin-film CdTe photovoltaic devices beyond 20% conversion efficiency , 2013 .

[9]  Wyatt K. Metzger,et al.  Grain-boundary recombination in Cu(In,Ga)Se2 solar cells , 2005 .

[10]  David Cahen,et al.  Stability of CdTe/CdS thin-film solar cells , 2000 .

[11]  Yanfa Yan,et al.  Effect of copassivation of Cl and Cu on CdTe grain boundaries. , 2008, Physical review letters.

[12]  Sidney R. Cohen,et al.  Electronically active layers and interfaces in polycrystalline devices: Cross-section mapping of CdS/CdTe solar cells , 2003 .

[13]  L. Kranz,et al.  Tailoring Impurity Distribution in Polycrystalline CdTe Solar Cells for Enhanced Minority Carrier Lifetime , 2014 .

[14]  Yanfa Yan,et al.  Characterization of extended defects in polycrystalline CdTe thin films grown by close-spaced sublimation , 2001 .

[15]  S. Asher,et al.  Phase control of CuxTe film and its effects on CdS/CdTe solar cell☆ , 2007 .

[16]  Jonathan D. Poplawsky,et al.  From atomic structure to photovoltaic properties in CdTe solar cells , 2013 .

[17]  G. Hahn,et al.  Detailed Investigation of Surface Passivation Methods for Lifetime Measurements on P-Type Silicon Wafers , 2011, IEEE Journal of Photovoltaics.

[18]  J. Ziegler,et al.  SRIM – The stopping and range of ions in matter (2010) , 2010 .

[19]  H. Fitting,et al.  Electron penetration and energy transfer in solid targets , 1977 .

[20]  H. Morgner,et al.  Effect of chlorine activation treatment on electron beam induced current signal distribution of cadmium telluride thin film solar cells , 2013 .

[21]  D. Bonnet,et al.  A comparative EBIC study of CdTe solar cell activation using CdCl2 and Cl2 , 2001 .

[22]  Shiro Nishiwaki,et al.  Doping of polycrystalline CdTe for high-efficiency solar cells on flexible metal foil , 2013, Nature Communications.

[23]  W. Brown,et al.  Chlorine-doped CdS thin films from CdCl2-mixed CdS powder , 2004 .

[24]  Mowafak Al-Jassim,et al.  Grain-boundary-enhanced carrier collection in CdTe solar cells. , 2014, Physical review letters.

[25]  Yanfa Yan,et al.  Passivation of double-positioning twin boundaries in CdTe , 2004 .

[26]  M. Young,et al.  CdCl2 treatment, S diffusion, and recombination in polycrystalline CdTe , 2006 .

[27]  W. Metzger,et al.  The impact of charged grain boundaries on thin-film solar cells and characterization , 2005 .

[28]  D. Cahen,et al.  How Polycrystalline Devices Can Outperform Single‐Crystal Ones: Thin Film CdTe/CdS Solar Cells , 2004 .

[29]  A. Tiwari,et al.  Analysis of Bulk and Interface Phenomena in CdTe/CdS Thin-Film Solar Cells , 2004 .

[30]  H. Queisser,et al.  Detailed Balance Limit of Efficiency of p‐n Junction Solar Cells , 1961 .

[31]  P. Sellin,et al.  EBIC and IBIC Imaging on Polycrystalline CdTe , 2007 .

[32]  J. Bonard,et al.  Quantitative analysis of electron-beam-induced current profiles across p-n junctions in GaAs/Al0.4Ga0.6As heterostructures , 1996 .

[33]  Wilhelm Warta,et al.  Solar cell efficiency tables (version 42) , 2013 .

[34]  T. Coutts,et al.  Development of Cu‐doped ZnTe as a back‐contact interface layer for thin‐film CdS/CdTe solar cells , 1996 .

[35]  Martin A. Green,et al.  Radiative efficiency of state‐of‐the‐art photovoltaic cells , 2012 .

[36]  Suhuai Wei,et al.  Electrically benign behavior of grain boundaries in polycrystalline CuInSe2 films. , 2007, Physical review letters.