Multilayer ZrO2 Precursor Coated Polystyrene Particles

Monodispersed ZrO2 (includes 8mol % Y2O3) precursor nanoparticles, which were well dispersed in aqueous solution, were successfully synthesized. The as-synthesized ZrO2 precursor nanoparticles were homogenously coated on the surface of polystyrene particles. Multilayer coating process was successfully implemented by using polyacrylic acid (PAA) to modify the surface charges of the coated particles, which was characterized by zeta-potential, particles size distribution and scanning electron microscopy (SEM).

L. Bergström | K. Watari | Y. Hotta | Kimiyasu Sato | Y. Jia

[1] L. Bergström,et al. Coated polystyrene particles as templates for ordered macroporous silica structures with controlled wall thickness , 2003 .

[2] F. Caruso,et al. Synthesis of macroporous titania and inorganic composite materials from coated colloidal spheres - A novel route to tune pore morphology. , 2001 .

[3] F. Caruso,et al. Hierarchical assembly of zeolite nanoparticles into ordered macroporous monoliths using core-shell building blocks. , 2000 .

[4] Andreas Stein,et al. Synthesis of highly ordered, three-dimensional, macroporous structures of amorphous or crystalline inorganic oxides, phosphates, and hybrid composites , 1999 .

[5] A. Stein,et al. Synthesis of macroporous minerals with highly ordered three-dimensional arrays of spheroidal voids , 1998, Science.

[6] J. Hilborn,et al. Chemically induced phase separation: a new technique for the synthesis of macroporous epoxy networks , 1996 .