Starburst DCM‐Type Red‐Light‐Emitting Materials for Electroluminescence Applications

Three new starburst DCM (4‐(dicyanomethylene)‐2‐methyl‐6‐[4‐(dimethylaminostyryl)‐4H‐pyran]) derivatives, 4,4′,4′′‐tris[2‐(4‐dicyanomethylene‐6‐t‐butyl‐4H‐pyran‐2‐yl)‐ethylene]triphenylamine (TDCM), 4,4′,′′‐tris[2‐(4‐(1′,3′‐indandione)‐6‐t‐butyl‐4H‐pyran‐2‐yl)‐ethylene]triphenylamine (TIN), and 4‐methoxy‐4′,4′′‐bis[2‐(4‐(1′,3′‐indandione)‐6‐t‐butyl‐4H‐pyran‐2‐yl)‐ethylene]triphenylamine (MBIN), have been designed and synthesized for application as red‐light emitters in organic light‐emitting diodes (OLEDs). Differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) reveal their extremely high glass‐transition temperatures and decomposition temperatures, as well as their low tendency to crystallize. Photoluminescence and electroluminescence measurements show that they exhibit a greatly restricted concentration‐quenching effect compared to DCM1 (4‐(dicyanomethylene)‐2‐methyl‐6‐[p‐(N,N‐dimethylamino)‐styryl]‐4H‐pyran), a simple but typical DCM‐type dye, as a result of their non‐planar, three‐dimensional structures that result from their unique propeller‐like triphenylamine electron‐donating cores. The peripheral electron‐withdrawing moieties also play a key role in the restriction of concentration quenching. That is, TIN and MBIN, bearing 1,3‐indandione acceptors, emit more efficiently than TDCM and DCM1, which have dicyanomethylene as acceptors at a high doping concentration of 10 wt.‐% in poly(9‐vinylcarbazole) (PVK) film, irrespective of whether they are photoexcited or electroexcited, though their fluorescence quantum yields in dilute solutions are much lower than that of DCM1. By way of the co‐doping approach, the electroluminescence device with the configuration indium tin oxide (ITO)/PVK:MBIN(10 wt.‐%):tris(4‐(2‐phenylethynyl)‐phenyl)amine (TPA; 30 wt.‐%) (70 nm)/2,9‐dimethyl‐4,7‐diphenyl‐1,10‐phenanthroline (BCP; 20 nm)/tris(8‐quinolinolato) aluminum (Alq3;15 nm)/LiF (0.3 nm)/Al (150 nm) exhibits a turn‐on voltage of 5.1 V, a maximum luminance of 6971 cd m–2, a maximum efficiency of 6.14 cd A–1 (405 cd m–2), and chromaticity coordinates of (0.66,0.33). The encouraging electroluminescence performance suggests potential applications of the starburst DCM red‐light emitters in OLEDs.