The Influence of PV Module Materials and Design on Solder Joint Thermal Fatigue Durability

Finite element model (FEM) simulations have been performed to elucidate the effect of flat plate photovoltaic (PV) module materials and design on PbSn eutectic solder joint thermal fatigue durability. The statistical method of Latin Hypercube sampling was employed to investigate the sensitivity of simulated damage to each input variable. Variables of laminate material properties and their thicknesses were investigated. Using analysis of variance, we determined that the rate of solder fatigue was most sensitive to solder layer thickness, with copper ribbon and silicon thickness being the next two most sensitive variables. By simulating both accelerated thermal cycles (ATCs) and PV cell temperature histories through two characteristic days of service, we determined that the acceleration factor between the ATC and outdoor service was independent of the variables sampled in this study. This result implies that an ATC test will represent a similar time of outdoor exposure for a wide range of module designs. This is an encouraging result for the standard ATC that must be universally applied across all modules.

[1]  R. Dudek,et al.  Solder fatigue acceleration prediction and testing results for different thermal test- and field cycling environments , 2014, Proceedings of the 5th Electronics System-integration Technology Conference (ESTC).

[2]  R. Subrahmanyan,et al.  A damage integral approach to thermal fatigue of solder joints , 1989, Proceedings., 39th Electronic Components Conference.

[3]  Ahmer Syed,et al.  Predicting solder joint reliability for thermal, power, and bend cycle within 25% accuracy , 2001, 2001 Proceedings. 51st Electronic Components and Technology Conference (Cat. No.01CH37220).

[4]  A. Syed.  Accumulated creep strain and energy density based thermal fatigue life prediction models for SnAgCu solder joints , 2004, 2004 Proceedings. 54th Electronic Components and Technology Conference (IEEE Cat. No.04CH37546).

[5]  N. Kelkar,et al.  Solder joint reliability model vath modified Darveaux's equations for the micro smd wafer level-chip scale package family , 2003, 53rd Electronic Components and Technology Conference, 2003. Proceedings..

[6]  Nick Bosco,et al.  Simulation and experiment of thermal fatigue in the CPV die attach , 2012 .

[7]  J. Wilde,et al.  Applying Anand Model to Represent the Viscoplastic Deformation Behavior of Solder Alloys , 2001 .

[8]  William E. Boyson,et al.  Photovoltaic array performance model. , 2004 .

[9]  W. Engelmaier,et al.  Generic reliability figures of merit design tools for surface mount solder attachments , 1993 .

[10]  Xuejun Fan,et al.  Effects of Dwell Time and Ramp Rate on Lead-Free Solder Joints in FCBGA Packages , 2005, Proceedings Electronic Components and Technology, 2005. ECTC '05..

[11]  Michael G. Pecht,et al.  Creep fatigue models of solder joints: A critical review , 2016, Microelectron. Reliab..

[12]  Haiyu Qi,et al.  Plastic ball grid array (PBGA) solder joint reliability assessment under combined thermal cycling and vibration loading conditions , 2006 .

[13]  W. K. Loh,et al.  Solder joint fatigue in a surface-mount assembly subjected to mechanical loading , 2005, 2005 7th Electronic Packaging Technology Conference.

[14]  Nick Bosco,et al.  Evaluation of Dynamic Mechanical Loading as an accelerated test method for ribbon fatigue , 2013, 2013 IEEE 39th Photovoltaic Specialists Conference (PVSC).

[15]  D. L. King,et al.  Commonly observed degradation in field-aged photovoltaic modules , 2002, Conference Record of the Twenty-Ninth IEEE Photovoltaic Specialists Conference, 2002..

[16]  R. Darveaux.  Effect of simulation methodology on solder joint crack growth correlation , 2000, 2000 Proceedings. 50th Electronic Components and Technology Conference (Cat. No.00CH37070).

[17]  D. L. King,et al.  Photovoltaic module performance and durability following long‐term field exposure , 2000 .

[18]  J. Miller,et al.  Long Term Reliability of Photovoltaic Modules , 2006, 2006 IEEE 4th World Conference on Photovoltaic Energy Conference.

[19]  H. Reichl,et al.  Fatigue life models for SnAgCu and SnPb solder joints evaluated by experiments and simulation , 2003, 53rd Electronic Components and Technology Conference, 2003. Proceedings..