论文信息 - THERMOMECHANICAL PROCESSING AND CONTINUOUS COOLING TRANSFORMATION BEHAVIOR OF IN-718

THERMOMECHANICAL PROCESSING AND CONTINUOUS COOLING TRANSFORMATION BEHAVIOR OF IN-718

The influence of homogenization treatment and cooling rates on the transformation characteristics of IN-718 alloy were studied. In addition, the effect of thermomechanical processing on the recrystallization behavior of this alloy was also investigated. The results of this investigation led to both the construction of continuous cooling transformation diagrams and to the establishment of a temperature-deformation-recrystallization map for this alloy.

[1] Greg K. Bouse. Application of a Modified Phase Diagram to the Production of Cast Alloy 718 Components , 1989 .

[2] A. D. Romig,et al. A comparison of the solidification behavior of INCOLOY 909 and INCONEL 718 , 1990 .

[3] J. Radavich. Metallography of Alloy 718 , 1988 .

[4] W. Cao,et al. Differential Thermal Analysis (DTA) Study of the Homogenization Process in Alloy 718 , 1991 .

[5] M. Miller,et al. Precipitation in Alloy 718 : A combined AEM and APFIM investigation , 1991 .

[6] A. J. DeArdo,et al. Microstructural Refinement of As-Cast Alloy 718 Via Thermomechanical Processing , 1991 .

[7] J. Radavich,et al. A Current T-T-T Diagram for Wrought Alloy 718 , 1991 .

[8] Y. C. Fayman. Microstructural characterization and elemental partitioning in a direct-aged superalloy (DA 718) , 1987 .

[9] A. D. Romig,et al. The solidification metallurgy of Alloy 718 and other Nb-containing superalloys , 1989 .

[10] A. D. Romig,et al. INCONEL 718: A solidification diagram , 1989 .