TiN/Cr/Al2O3 and TiN/Al2O3 hybrid coatings structure features and properties resulting from combined treatment

Abstract New experimental results are presented on the structure and the elemental and phase composition of hybrid coatings, which were deposited on a substrate of AISI 321 stainless steel using a combination of plasma-detonation, vacuum-arc and subsequent High-Current Electron Beam (HCEB) treatment. We found that an increase in energy density intensified mass transfer processes and resulted in changes in aluminum oxide phase composition (γ → α and β → α). Also we observed the formation of a nanocrystalline structure in Al 2 O 3 coatings. Electron beam treatment of a hybrid coating surface induced higher adhesion, decreased the intensity of surface wear and increased corrosion resistance in a sulphuric acid solution. The corrosion resistance of the coatings was studied in several electrolytic solutions (0.5 M H 2 SO 4 , 1 M HCl, 0.75 M NaCl) using electrochemical techniques. In most cases the corrosion resistance was improved, except those in NaCl solutions. The nano-hardness of the protecting coating was 13 GPa before electron beam melting and 9 GPa after it (as a result of TiN and Al 2 O 3 sub-layers mixing).