The effect of the melt spinning processing parameters on the solidification structures in Ti–30 at.% Ni–20 at.% Cu shape memory alloys

Abstract Solidification structures and shape memory characteristics of Ti–30 at.% Ni–20 at.% Cu alloy ribbons prepared by melt spinning were investigated by means of differential scanning calorimetry and X-ray diffraction. In these experiments particular attention has been paid to change the ejection temperature of the melt from 1350 to 1500 °C and the velocity of cooling wheel from 33 to 55 m/s. Then the cooling rates of ribbons were controlled. The effect of this cooling rate on solidification structures and martensitic transformation behaviors is discussed.

[1] T. Nam,et al. Cu-Content Dependence of Shape Memory Characteristics in Ti–Ni–Cu Alloys , 1990 .

[2] T. W. Duerig,et al. Engineering Aspects of Shape Memory Alloys , 1990 .

[3] G. Fulcher,et al. ANALYSIS OF RECENT MEASUREMENTS OF THE VISCOSITY OF GLASSES , 1925 .

[4] O. Mercier,et al. The substitution of Cu for Ni in NiTi shape memory alloys , 1979 .

[5] Y. Furuya,et al. Thermo-mechanical Phase Transformation of Rapidly Quenched Ti–Ni–Cu Ribbons , 1990 .

[6] Tae Hyun Nam,et al. The Effect of Rapidly Solidified Microstructures on the Martensitic Transformation in Ti50-Ni45-Cu5 Shape Memory Alloys , 2005 .

[7] D. Turnbull. Under what conditions can a glass be formed , 1969 .