Evaluation of arc ion plated NiCoCrAlYSiB coatings after oxidation at 900–1100 °C
暂无分享,去创建一个
P. Ke | Qisheng Wang | J. Gong | Congting Sun | L. Wen | Fuguo Wang | Yaorong Wu
[1] P. Ke,et al. Hot corrosion behavior of AIP NiCoCrAlY(SiB) coatings on nickel base superalloys , 2004 .
[2] S. Gong,et al. Thermal cycling behaviors of thermal barrier coatings on intermetallic Ni3Al based superalloy , 2003 .
[3] L. Singheiser,et al. Analysis of corrosion layers on protective coatings and high temperature materials in simulated service environments of modern power plants using SNMS, SIMS, SEM, TEM, RBS and X-ray diffraction studies , 2002, Analytical and bioanalytical chemistry.
[4] A. Marder,et al. Oxidation of Ni–Al-Base Electrodeposited Composite Coatings. I: Oxidation Kinetics and Morphology at 800°C , 2002 .
[5] Aiying Wang,et al. Oxidation behaviour of NiCrAlY coatings on Ni-based superalloy , 2002 .
[6] J. Gong,et al. Interdiffusion Behavior of Ni–Cr–Al–Y Coatings Deposited by Arc-Ion Plating , 2001 .
[7] I. Gurrappa,et al. Identification of hot corrosion resistant MCrAlY based bond coatings for gas turbine engine applications , 2001 .
[8] F. Wu,et al. Evaluation of NiCrAlYSi overlay coating on Ni3Al based alloy IC-6 after an engine test , 1999 .
[9] R. A. Reich,et al. Boundary Additive Effect on Abrasive Wear During Single Asperity Plowing of a 3004 Aluminum Alloy , 1999 .
[10] W. Quadakkers,et al. TEM and SNMS studies on the oxidation behaviour of NiCrAlY-based coatings , 1997 .
[11] A. Petric,et al. Oxidation ofγ′-Ni3Al andγ′-Ni3Al(Si) intermetallic compounds at low-oxygen pressures , 1996 .
[12] B. Pint. Experimental observations in support of the dynamic-segregation theory to explain the reactive-element effect , 1996 .
[13] S. Shi,et al. Oxidation of γ-Ni−Al−Si alloys at 1073 K , 1995 .
[14] M. Winstone,et al. Hot corrosion resistance of coated single crystal superalloys under marine conditions , 1993 .
[15] B. Champagne,et al. Oxidation and Hot Corrosion in Na2SO4–10%V2O5 of Ni–17Cr–6Al–0.5Y and Ni–16Cr–5.7Al–0.47Y–5Si MCrAly Alloys at 700°C , 1991 .
[16] P. Nanni,et al. Erratum: The transition from internal oxidation to continuous film formation during oxidation of dilute Ni-Si alloys , 1987 .
[17] R. Bauer,et al. The role of silicon in corrosion-resistant high temperature coatings , 1982 .
[18] C. Barrett,et al. The Effect of Zirconium on the Isothermal Oxidation of Nominal Ni ‐ 14Cr ‐ 24Al Alloys , 1980 .
[19] G. Wahl,et al. The properties of a chemical vapour-deposited silicon base coating for gas turbine blading , 1979 .
[20] J. Tien,et al. Mechanism of oxide adherence on Fe-25Cr-4Al (Y or Sc) alloys , 1972 .