Effects of Gas Adsorption on the Mechanical Properties of Amorphous Polymer

This study investigates the properties of a polymer–gas mixture formed through diffusion, based on the changes in the partial pressure and observed changes in the impact and tensile strengths owing to the gas dissolution. The high-pressure gas dissolves into a solid-state polymer through diffusion based on the difference in the partial pressure. This dissolved gas is present in the amorphous region within the polymeric material temporarily, which results in the polymer exhibiting different mechanical properties, while the gas remains dissolved in the polymer. In this study, the mechanical properties of amorphous polyethylene terephthalate (APET) specimens prepared by dissolving CO2 using a high-pressure vessel were investigated, and the resulting impact and tensile strengths were measured. These experiments showed that the increase in sorption rate of CO2 caused an increase in the impact strength. At 2.9% CO2 absorption, the impact strength of APET increased 956% compared to that of the reference specimen. Furthermore, the tensile strength decreased by up to 71.7% at 5.48% CO2 sorption; the stress–strain curves varied with the gas sorption rate. This phenomenon can be associated with the change in the volume caused by CO2 dissolution. When the APET absorbed more than 2.0% CO2 gas, sample volume increased. A decrease in the network density can occur when the volume is increased while maintaining constant mass. The CO2 gas in the polymer acted as a cushion in impact tests which have sorption rates above 2%. In addition to the reduction in the network density in the polymer chain, Van Der Waals forces are decreased causing a decrease in tensile strength only while CO2 is present in the APET. These observations only occur prior to CO2 desorption from the polymer.

[1]  Chul B. Park,et al.  Dimethyl ether’s plasticizing effect on carbon dioxide solubility in polystyrene , 2016 .

[2]  Ronald P White,et al.  Polymer Free Volume and Its Connection to the Glass Transition , 2016 .

[3]  C. Xin,et al.  Study of volume swelling and interfacial tension of the polystyrene-carbon dioxide-dimethyl ether system. , 2015, Journal of colloid and interface science.

[4]  Ying-Hui Qian,et al.  Experimental Study of the Synergistic Plasticizing Effect of Carbon Dioxide and Ibuprofen on the Glass Transition Temperature of Poly(methyl methacrylate) , 2014 .

[5]  Dujing Wang,et al.  Stress induced lamellar thickening in poly(ethylene succinate) , 2013 .

[6]  S. Kim,et al.  Investigation of Properties of the PET Film Dependent on the Biaxial Stretching , 2010 .

[7]  W. Yuan,et al.  Solubility and Diffusivity of Carbon Dioxide in Solid-State Isotactic Polypropylene by the Pressure−Decay Method , 2009 .

[8]  M. Tuttle,et al.  Effect of CO2 sorption and desorption on the creep response of polycarbonate , 2005 .

[9]  Heh Han Meijer,et al.  On the origin of strain hardening in glassy polymers , 2003 .

[10]  S. Cha,et al.  Change of Glass Transition Temperature of PETG Containing Gas , 2000 .

[11]  Karl A. Seeler,et al.  Experimental Characterization of the Tensile Behavior of Microcellular Polycarbonate Foams , 1994 .

[12]  Sung Woon Cha,et al.  A microcellular foaming/forming process performed at ambient temperature and a super-microcelluar foaming process , 1994 .

[13]  Daniel Flanagan Baldwin,et al.  Microcellular polymer processing and the design of a continuous sheet processing system , 1994 .

[14]  Chul B. Park,et al.  The role of polymer/gas solutions in continuous processing of microcellular polymers , 1993 .

[15]  J. Sauer Deformation, yield and fracture of polymers at high pressure , 1977 .