Using a cohesive damage model to predict the tensile behaviour of CFRP single-strap repairs

This work addresses both experimental and numerical analyses regarding the tensile behaviour of CFRP single-strap repairs. Two fundamental geometrical parameters were studied: overlap length and patch thickness. The numerical model used ABAQUS® software and a developed cohesive mixed-mode damage model adequate for ductile adhesives, and implemented within interface finite elements. Stress analyses and strength predictions were carried out. Experimental and numerical comparisons were performed on failure modes, failure load and equivalent stiffness of the repair. Good correlation was found between experimental and numerical results, showing that the proposed model can be successfully applied to bonded joints or repairs.

[1]  Peter Davies,et al.  A study of the non-linear behaviour of adhesively-bonded composite assemblies , 2006 .

[2]  Laurent Champaney,et al.  A damage-mechanics-based approach for modelling decohesion in adhesively bonded assemblies , 2006 .

[3]  Ulf Stigh,et al.  Shear behaviour of adhesive layers , 2007 .

[4]  Michael R Wisnom,et al.  Shape optimisation of adhesive fillets , 2000 .

[5]  Viggo Tvergaard,et al.  On the toughness of ductile adhesive joints , 1996 .

[6]  Jiye Chen,et al.  Predicting Progressive Delamination of Stiffened Fibre-Composite Panel and Repaired Sandwich Panel by Decohesion Models , 2002 .

[7]  Erdogan Madenci,et al.  Influence of adhesive spew in bonded single-lap joints , 2006 .

[8]  Chun-Gon Kim,et al.  Failure mode and strength of uni-directional composite single lap bonded joints with different bonding methods , 2006 .

[9]  M. D. Thouless,et al.  Mixed-mode fracture analyses of plastically-deforming adhesive joints , 2001 .

[10]  Z. Suo,et al.  Mixed mode cracking in layered materials , 1991 .

[11]  A. T. Marques,et al.  Modeling Compression Failure after Low Velocity Impact on Laminated Composites Using Interface Elements , 1997 .

[12]  Ulf Stigh,et al.  An explicit FE-model of impact fracture in an adhesive joint , 2007 .

[13]  Dong-Hyun Kim,et al.  Failure of carbon composite-to-aluminum joints with combined mechanical fastening and adhesive bonding , 2006 .

[14]  M. D. Thouless,et al.  The effects of geometry and material properties on the fracture of single lap-shear joints , 2002 .

[15]  Constantinos Soutis,et al.  Strength prediction of patch-repaired CFRP laminates loaded in compression , 2000 .

[16]  M. D. Thouless,et al.  Use of a cohesive-zone model to analyze the fracture of a fiber-reinforced polymer-matrix composite , 2005 .

[17]  M. D. Thouless,et al.  Elastic–plastic mode-II fracture of adhesive joints , 2001 .

[18]  M. D. de Moura,et al.  Stress and failure analyses of scarf repaired CFRP laminates using a cohesive damage model , 2007 .

[19]  Ulf Stigh,et al.  The stress–elongation relation for an adhesive layer loaded in peel using equilibrium of energetic forces , 2004 .

[20]  A. Waas,et al.  Mixed-mode cohesive-zone models for fracture of an adhesively bonded polymer–matrix composite , 2006 .

[21]  J. Hutchinson,et al.  The influence of plasticity on mixed mode interface toughness , 1993 .

[22]  M. D. Thouless,et al.  Numerical simulations of adhesively-bonded beams failing with extensive plastic deformation , 1999 .

[23]  M. D. Moura,et al.  Modelling single and double-lap repairs on composite materials , 2005 .

[24]  M. D. Thouless,et al.  Use of mode-I cohesive-zone models to describe the fracture of an adhesively-bonded polymer-matrix composite , 2005 .

[25]  T. Andersson,et al.  On the effective constitutive properties of a thin adhesive layer loaded in peel , 2006 .