A revised interpretation of ultra-fast stress corrosion cracking experiments by Serebrinsky and Galvele

[1]  R. Newman,et al.  Film-Induced Cleavage of Ag-Au Alloys , 2009 .

[2]  S. Corcoran,et al.  Probing the Dealloying Critical Potential Morphological Characterization and Steady-State Current Behavior , 2005 .

[3]  J. Galvele,et al.  Stress corrosion cracking of copper and silver, specific effect of the metal cations , 2005 .

[4]  J. Erlebacher.  An Atomistic Description of Dealloying Porosity Evolution, the Critical Potential, and Rate-Limiting Behavior , 2004 .

[5]  J. Galvele,et al.  Effect of the strain rate on stress corrosion crack velocities in face-centred cubic alloys. A mechanistic interpretation , 2004 .

[6]  R. Newman.  Stress-Corrosion Cracking Mechanisms , 2002 .

[7]  J. Galvele,et al.  The stress corrosion cracking of AgAu alloys—I. 1 M perchloric acid solution , 1995 .

[8]  J. Galvele,et al.  Stress corrosion cracking of Ag-20Au in HCLO4, AgCLO4, and KCL solutions by surface mobility , 1993 .

[9]  K. Sieradzki,et al.  Stress‐Corrosion Cracking of Alpha‐Brass Without Copper Oxidation , 1993 .

[10]  A. Young,et al.  The Characterization of the Coarsening of Dealloyed Layers by EIS and Its Correlation with Stress-Corrosion Cracking , 1993 .

[11]  R. Newman,et al.  Testing the film-induced cleavage model of stress-corrosion cracking , 1993 .

[12]  R. C. Newman,et al.  The Relationship Between Dealloying and Transgranular Stress-Corrosion Cracking of Cu-Zn and Cu-Al Alloys , 1987 .

[13]  K. Sieradzki,et al.  Film-Induced Cleavage During Stress-Corrosion Cracking of Ductile Metals and Alloys , 1987 .

[14]  K. Sieradzki,et al.  Stress Corrosion Cracking , 2001 .

[15]  K. Sieradzki,et al.  Brittle behavior of ductile metals during stress-corrosion cracking , 1985 .