Fracture anisotropy in silicon single crystal

In this study the effect of crystallographic orientation on fracture toughness and the fracture path of silicon single crystal was investigated. Vickers microhardness indentation was used to introduce cracks along various crystallographic orientations on the (110), (001), and (111) planes. The fracture toughness variation was found to follow the symmetry of the indentation axis with no distinct correlation with the elastic constants. The observations made suggest that the inclination angle of cleavage planes relative to the indent plane affects the fracture path and toughness significantly. Prestraining decreased the hardness and improved the toughness without a modification of fracture path.

[1]  Gérard Michot,et al.  Dislocation loops at crack tips: nucleation and growth— an experimental study in silicon , 1993 .

[2]  R. J. Jaccodine,et al.  Surface Energy of Germanium and Silicon , 1963 .

[3]  K. Niihara,et al.  A fracture mechanics analysis of indentation-induced Palmqvist crack in ceramics , 1983 .

[4]  David R. Clarke,et al.  Direct observation of dislocation emission from crack tips in silicon at high temperatures , 1989 .

[5]  C. John.  The brittle-to-ductile transition in pre-cleaved silicon single crystals , 1975 .

[6]  Kunio Hayashi,et al.  Fracture toughness of single crystal silicon. , 1991 .

[7]  J. Gilman,et al.  Direct Measurements of the Surface Energies of Crystals , 1960 .

[8]  J. B. O'Neill,et al.  Anisotropy in the hardness of single crystals , 1971, Proceedings of the Royal Society of London. A. Mathematical and Physical Sciences.

[9]  P. Warren,et al.  Knoop hardness anisotropy on {001} faces of germanium and gallium arsenide , 1986 .

[10]  S. Danyluk,et al.  Surface Free Energy Model of Silicon Anisotropic Etching , 1993 .

[11]  J. Schweitz,et al.  Contact Damage in Single‐Crystalline Silicon Investigated by Cross‐Sectional Transmission Electron Microscopy , 1988 .

[12]  F. Ebrahimi,et al.  Nature of slip during knoop indentation on “100” surface of NiAl , 1996 .

[13]  S. Roberts,et al.  Indentation plasticity and polarity of hardness on {111} faces of GaAs , 1985 .

[14]  M. Brede,et al.  The brittle-to-ductile transition in doped silicon as a model substance , 1988 .

[15]  D. Callahan,et al.  The extent of phase transformation in silicon hardness indentations , 1992 .

[16]  J. J. Mecholsky,et al.  Fractal fracture of single crystal silicon , 1991 .

[17]  Stephen Roberts,et al.  The brittle-ductile transition in silicon. II. Interpretation , 1989, Proceedings of the Royal Society of London. A. Mathematical and Physical Sciences.