Inhibiting effect of octadecylamine on pitting corrosion behaviour of stainless steel type 1.4541 up to 250 °C

The inhibiting effect of octadecyclamine (ODA) on chloride induced localized corrosion of austenitic stainless steel type 1.4541 (AISI 321) is described at temperatures from 150 °C and 250 °C indeaerated aqueous solutions with chloride concentrations up to 10- 1 M. Results of electrochemical (current-potentiAl-curves, impedance spectroscopy) as well as corrosion tests on mechanical loaded samples (constant extension rate test), and surface analytical characterization (Auger electron spectroscopy) showed the inhibiting effect of ODA. The increase of the corrosion resistance of the investigated material is interpreted by an ODA-film on steel surface as a diffusion barrier, and the formation of a compact hot-water oxide layer, caused by the increase of pH resulted from ODA-cracking and dissociation. Inhibierender Effekt von Octadecylamin auf das Lochkorrosionsverhalten des Stahles 1.4541 bis 250 °C Es wird die inhibierende Wirkung von Octadecylamin (ODA) auf die chloridinduzierte lokale Korrosion des austenitischen Stahls 1.4541 bei Temperaturen von 150 °C und 250 °C in entlufteten Losungen mit Chloridkonzentrationen bis 10- 1 mol/l beschrieben. Aus den Ergebnissen der elektrochemischen Tests (Stromdichte-PotentiAl-Kurven, Impedanzspektroskopie), Korrosionsuntersuchungen bei mechanischer Belastung (constant extension rate test) und oberflachenanalytischer Charakterisierung (Augerelektronenspektroskopie) zeigte sich, das ODA die Korrosionsresistenz des untersuchten Werkstoffes erhoht. Die erhohte Korrosionsresistenz wird einer Diffusionsbarriere durch einen ODA-Film auf der Stahloberflache und durch die Ausbildung einer kompakten Heiswasseroxidschicht infolge der aus der ODA-Zersetzung und -Dissoziation resultierenden pH-Wert-Erhohung zugeschrieben.