CHLORIDE DIFFUSION AND REINFORCEMENT CORROSION IN MARINE EXPOSED CONCRETE CONTAINING PULVERIZED-FUEL ASH. CORROSION OF REINFORCEMENT IN CONCRETE. PAPERS PRESENTED AT THE THIRD INTERNATIONAL SYMPOSIUM ON "CORROSION OF REINFORCEMENT IN CONCRETE CONSTRUCTION", BELFRY HOTEL, WISHAW, WARWICKSHIRE, MAY 21
暂无分享,去创建一个
Steel reinforced concrete specimens, with pulverized-fuel ash (pfa) contents in the range 0 to 50% and designed to equal strength grade and workability, were exposed in the tidal zone of the BRE seawater exposure site following various periods of initial curing. Total chloride concentration profiles and reinforcement bar weight losses were determined on specimens retrieved after exposure periods of 1 and 2 years. Chloride diffusion coefficients were calculated from the chloride concentration data. The results show that in both pfa (pulverized fuel ash) concrete and opc (ordinary portland cement) concrete the rate of penetration of chloride ions and subsequent corrosion of steel reinforcement are increased as the duration of initial curing is curtailed. However, these effects become less pronounced as the length of exposure is extended. Both the rate of penetration of chloride ions and the consequent weight loss of reinforcing bars due to corrosion are lower in pfa concrete than in the control opc concrete and decrease with increasing pfa content. For all specimens a correlation was established between reinforcing bar weight loss and total chloride concentration at the location of the steel, enabling a threshold value for chloride content to initiate corrosion to be determined.(A) For the covering abstract of the conference see IRRD 831449.